The invention relates to a preparation method of decorative building ecological brick with color surface. The ecological brick refers to the utilization of fly ash, tailings slag, natural sand, seashore mud, etc. As the main raw material, using cement and additives as coagulant, the decorative surface of the outer layer of the brick is beautified by multi-mixture extrusion and high-pressure composite moulding of the brick billet. A new type of decorative ecological brick with color surface is made without calcination at high temperature. It has high strength, good product performance and relatively environmental protection. The country has been vigorously promoting it. It can be applied to building, hall, villa and other wall material bricks, but also plays a decorative role on the external wall.
【技术实现步骤摘要】
一种彩面装饰建筑生态砖的制配方法
:本专利技术属于建筑装饰材料
,具体涉及一种彩面装饰建筑生态砖的制配方法。
技术介绍
:众所周知,随着社会的进步发展,对建筑装饰领域提出更新的要求,它不仅要强度高、耐腐蚀、防分化渗透能力强,而且要求绿色环保、美观大方,而现市场上的砖单调,而且不能节能环保,不符合社会发展的需求。
技术实现思路
:本专利技术的目的是根据上述的不足而提供一种彩面装饰建筑生态砖的制配方法。本专利技术的彩面装饰建筑生态砖的制配方法是利用石粉、水泥、砂石、粉煤灰、煤渣、煤矿石、矿渣、化工渣、天然砂、海涂泥为主要原料,用水泥做凝固剂,加以早强剂、减水剂、促凝剂、促发剂、防冻剂为添加剂,再加入氧化铁红、氧化铁黄、氧化铁黑、铬黄、铬绿无机颜料中一种或几种混合物。本专利技术的彩面装饰建筑生态砖是由彩色长边(1)与彩色宽边(2)砖体(3)构成,该砖体(1)的彩色宽边(2)、长边(1)是用石粉、水泥、砂石、添加剂、混合挤压成坯构成,彩色宽边(2),长边(1)可根据需求调加各种不同颜色的颜料,挤压复合成彩面装饰建筑生态砖体(1),该产品的砖是利用石粉、水泥、砂石、粉煤灰、煤渣、煤矿石、矿渣、化工渣、天然砂、海涂泥为主要原料其比例为40%-80%,用水泥做凝固剂量为10%-30%,添加剂早强剂量2%-8%、减水剂量为2%-8%、促凝剂量为2%-6%、促发剂量为2%-6%、防冻剂量为1%~6%,再加入氧化铁红、氧化铁黄、氧化铁黑、铬黄、铬绿无机颜料中一种或几种混合物,其量为1%-4%。本专利技术的彩面装饰建筑生态砖是采用废物煤渣、煤矸石、矿碴压制而成,它可变废为宝, ...
【技术保护点】
1.一种彩面装饰建筑生态砖的制配方法,其特征是利用石粉、水泥、砂石、粉煤灰、煤渣、煤矿石、矿渣、化工渣、天然砂、海涂泥为主要原料,其比例为40%‑80%,用水泥做凝固剂量为10%‑30%,添加剂以早强剂量2%‑8%、减水剂量为2%‑8%、促凝剂量为2%‑6%、促发剂量为2%‑6%、防冻剂量为1%‑6%,再加入氧化铁红、氧化铁黄、氧化铁黑、铬黄、铬绿无机颜料中一种或几种混合物,其量为1%‑4%。
【技术特征摘要】
1.一种彩面装饰建筑生态砖的制配方法,其特征是利用石粉、水泥、砂石、粉煤灰、煤渣、煤矿石、矿渣、化工渣、天然砂、海涂泥为主要原料,其比例为40%-80%,用水泥做凝固剂量为10%-30%,添加剂以早强剂量2%-8%、减水剂量为2%-8%、促凝剂量为2%-6%、促发剂量为2%-6%、防冻剂量为1%-6%,再加入氧化...
【专利技术属性】
技术研发人员:胡泽军,
申请(专利权)人:湖南江山飞龙新材料科技有限公司,湖南天工生态环境科技有限公司,
类型:发明
国别省市:湖南,43