The invention discloses a sugar battery anode catalyst containing nickel, cobalt and nitrogen, and its preparation method and application. The preparation method of the sugar battery anode catalyst containing nickel, cobalt and nitrogen includes the following steps: taking cobalt nitrate, nickel nitrate, urea, ethanol and mint powder, mixing evenly; stirring; and cooling the sugar battery anode containing nickel, cobalt and nitrogen for 6-8 hours at 370-420 (?) and room temperature to obtain the sugar battery anode containing nickel, cobalt and nitrogen. Catalyzer. The preparation method of the invention is simple and feasible. The catalyst of the invention can be used to prepare a sugar battery anode with low cost, high efficiency and non-noble metal. The electrochemical properties of metals were significantly improved by adding nitrogen content. Sugar cell anode prepared with nickel-cobalt-nitrogen anode catalyst showed a maximum power density of 30.89W/m.
【技术实现步骤摘要】
含镍钴氮的糖电池阳极催化剂及制备方法和应用
本专利技术属于燃料电池催化剂领域，涉及一种含镍钴氮的糖电池阳极催化剂及制备方法和用途。
技术介绍
由于化石燃烧，人口增长，全球工业化和城市化加剧，环境空气污染日益严重，全球平均温度日益增加。天然气，汽油，煤和石油等化石燃料的燃烧是产生二氧化碳的主要来源，最终导致全球变暖。必须开发新的清洁能源，以满足全球能源需求，而不会产生二氧化碳。为了克服这些环境威胁，应该开发环保的可再生能源并发展减少二氧化碳排放的技术。因此，为了满足日益增长的无污染能源的需求，研究人员正在研究无毒和更多可用的燃料，人们对甲醇，乙醇和葡萄糖等生物燃料电池有了更多的追求。其中，葡萄糖、蔗糖等糖类物质是一种可再生的生物燃料，可大量供应，并且很容易从不同农业活动产生的废物生物质中获得。此外，糖类物质具有释放能量的能力。为了在糖中有效地获得储存的能量，直接将化学能转化为电能是可选的。燃料电池是将生物燃料中储存的化学能转化为电能的装置，以糖为底物的燃料电池(糖电池)由于其低排放，高稳定性和高效率等专有特性而备受关注。文献中已经有对直接碱性燃料电池(DAFC)进行...
【技术保护点】
1.含镍钴氮的糖电池阳极催化剂的制备方法，其特征是包括如下步骤：按比例取720‑870mg硝酸钴、720‑870mg硝酸镍、660‑750mg尿素、6‑8ml乙醇和50mg～80mg薄荷粉，混合均匀；搅拌10～12小时；在370℃～420℃下，通入氮气6～8小时，冷却至室温，得到含镍钴氮的糖电池阳极催化剂。
【技术特征摘要】
1.含镍钴氮的糖电池阳极催化剂的制备方法，其特征是包括如下步骤：按比例取720-870mg硝酸钴、720-870mg硝酸镍、660-750mg尿素、6-8ml乙醇和50mg～80mg薄荷粉，混合均匀；搅拌10～12小时；在370℃～420℃下，通入氮气6～8小时，冷却至室温，得到含镍钴氮的糖电池阳极催化剂。2.根据权利要求1所述的方法，其特征是所述硝酸钴、硝...
【专利技术属性】
技术研发人员：刘宪华，武蓝，任俊，易方，
申请(专利权)人：天津大学，
类型：发明
国别省市：天津,12