本发明专利技术提供一种穿刺强度高、能够实现薄膜化、高气孔率化的非水电解质二次电池用间隔件。非水电解质二次电池10具备电极体3和非水电解质，所述电极体3由正极20、负极30和间隔件40构成。间隔件40由按照A层41、B层42、C层43的顺序层叠而成的至少3层结构的多孔树脂片构成，A层41和C层43的0℃～50℃时的平均热膨胀系数比B层42的0℃～50℃时的平均热膨胀系数小100ppm/K以上。

Spacer for non-aqueous electrolyte secondary batteries and non-aqueous electrolyte secondary batteries

The invention provides a spacer for non-aqueous electrolyte secondary battery with high puncture strength, film forming and high porosity. The non-aqueous electrolyte secondary battery 10 has an electrode body 3 and a non-aqueous electrolyte. The electrode body 3 consists of a positive 20, a negative 30 and a spacer 40. The spacer 40 consists of at least three layers of porous resins laminated in the order of layer A 41, layer B 42 and layer C 43. The average thermal expansion coefficients of layer A 41 and layer C 43 at 0-50 C are less than 100 ppm/K at 0-50 C of layer B 42.

【技术实现步骤摘要】
非水电解质二次电池用间隔件和非水电解质二次电池
本申请涉及非水电解质二次电池用间隔件和非水电解质二次电池。
技术介绍
锂离子电池等非水电解质二次电池的电极体中使用间隔件，所述间隔件是具有离子透过性和绝缘性的多孔树脂片。例如，专利文献1公开了一种间隔件，其由多孔层叠膜构成，所述多孔层叠膜包含：由重均分子量为66万～98万的聚丙烯形成的多孔聚丙烯层、以及含有熔点为100℃～140℃这一范围的材料的多孔层，所述间隔件的针贯穿强度为470gf～510gf。此外，专利文献2公开了一种间隔件，其是具有形成两个表面层的第一多孔层以及设置在两个表面层之间的第二多孔层的聚烯烃多层微多孔膜，第一多孔层由超高分子量聚乙烯构成，第二多孔层由超高分子量聚乙烯和高密度聚乙烯构成。现有技术文献专利文献专利文献1：日本特许第3939778号专利文献2：日本特许第5202866号
技术实现思路
专利技术要解决的问题然而，对非水电解质二次电池要求进一步的高容量化、高输出化。对于作为二次电池的构成部件之一的间隔件而言，用于实现高容量化的薄膜化、用于实现高输出化的高气孔率化成为趋势，确保间隔件的强度成为课题。如果间隔件的强度变本文档来自技高网...

【技术保护点】
1.一种非水电解质二次电池用间隔件，其由按照A层、B层、C层的顺序层叠而成的至少3层结构的多孔树脂片构成，所述A层的0℃～50℃时的平均热膨胀系数比所述B层的0℃～50℃时的平均热膨胀系数小100ppm/K以上，所述C层的0℃～50℃时的平均热膨胀系数比所述B层的0℃～50℃时的平均热膨胀系数小100ppm/K以上。