The invention discloses a preparation process of an environment-friendly durable building material, which consists of 100 Portland cement, 30-40 volcanic ash, 300-400 sand grains, 5-10 aggregates, 10-15 antifreeze, 15-20 xanthan gum, 2-4 water reducers and 30-50 water. The preparation process includes the following steps: S1, anti-freezing. Preparation of frozen agent; S2, preparation of raw materials; S3, preparation of building materials. The building material provided by the invention has the advantages of durability, environmental protection, high strength, good impermeability, strong bonding force, long service life, easy transportation and construction, and short construction period.
【技术实现步骤摘要】
一种环保耐久型建筑材料的制备工艺
本专利技术涉及建筑材料
，尤其涉及一种环保耐久型建筑材料的制备工艺。
技术介绍
建筑材料是指由胶凝材料将集料胶结成整体的工程复合材料的统称，是工程建设中使用频率较高的材料之一。目前我们使用的建筑材料主要是用水泥作胶凝材料，加入砂、石作集料，再加一定比例的水搅拌而成的。建筑材料的性能将直接影响着建筑物的牢固度，尤其是建筑材料的抗冻性能和抗渗性能，所以建筑材料的发展逐渐朝向环保耐久型混合凝土方向进行。CN201811243132提出了石墨尾矿混凝土拌合物及其制备工艺，涉及建筑材料
，为了解决石墨尾矿污染环境、建筑用砂匮乏的问题。混凝土拌合物由346.15份水泥、1284.1份石子、330.20～550.33份砂子、59.97～239.88份石墨尾矿、1～1.3份减水剂和180份水制成。制备工艺：步骤一、配置原料；步骤二、将原料搅拌混合均匀，养护处理，得到石墨尾矿混凝土拌合物。本专利技术的混凝土强度高，本专利技术为污染物石墨尾矿的处理提供了一种新的处理方式，减少了环境污染，解决建筑用砂量的匮乏的问题。CN2018111876...
【技术保护点】
1.一种环保耐久型建筑材料的制备工艺，其特征在于，所述建筑材料由以下重量份的原料组成：硅酸盐水泥100份，火山灰30～40份，砂粒300～400份，骨料5～10份，防冻剂10～15份，黄原胶15～20份，减水剂2～4份，水30～50份；所述防冻剂由防冻组分A和亚硝酸钠构成，其中，防冻剂中防冻组分A和亚硝酸钠的质量比为1:3，防冻组分A的结构式如下：
【技术特征摘要】
1.一种环保耐久型建筑材料的制备工艺，其特征在于，所述建筑材料由以下重量份的原料组成：硅酸盐水泥100份，火山灰30～40份，砂粒300～400份，骨料5～10份，防冻剂10～15份，黄原胶15～20份，减水剂2～4份，水30～50份；所述防冻剂由防冻组分A和亚硝酸钠构成，其中，防冻剂中防冻组分A和亚硝酸钠的质量比为1:3，防冻组分A的结构式如下：所述制备工艺包括以下步骤：S1、防冻剂的制备：将防冻组分A和亚硝酸钠按照比例混合，进行机械搅拌至均匀，得防冻剂；S2、准备原料：按照硅酸盐水泥100份，火山灰30～40份，砂粒300～400...