A method for preparing magnetic nanowires is as follows: 1. preparing metal ion solution, alkali solution and water-soluble reductant solution; 2. mixing metal ion solution, alkali solution and water-soluble reductant solution into a reactor and reacting in a magnetic field heat treatment furnace; 3. washing and drying, i.e., obtaining magnetic nanowires. The invention solves the problems of complex operation, high cost and low nanowire yield of the existing preparation methods of Fe3O4 nanowires and spinel ferrite nanowires. The preparation method has the advantages of simple operation, no pollution to the environment and low cost. The yield of magnetic nanowires is 95.6-99.9%. It is applied in the field of magnetic materials.
【技术实现步骤摘要】
一种磁性纳米线的制备方法
本专利技术属于纳米线制备
，具体涉及一种磁性纳米线的制备方法。
技术介绍
现有的纳米线种类很多，磁性纳米线作为纳米材料的成员之一因其优异的磁学性能而得到广泛的应用。其中磁性Fe3O4纳米线和尖晶石型铁酸盐纳米线在磁性记录介质、光催化、磁流体、颜料染料等许多领域都有重要的应用价值。目前磁性Fe3O4纳米线和尖晶石型铁酸盐纳米线的制备方法中，溶胶-凝胶法和采用磁场辅助的水热方法所获得的纳米线产率较低，纳米线直径范围较广，且产物中常含有大量的纳米颗粒，品质较差。
技术实现思路
本专利技术针对上述现有技术存在的问题和不足，提供一种磁性纳米线的制备方法。本专利技术的一种磁性纳米线的制备方法，按以下步骤进行：一、用蒸馏水、三氯化铁和二价金属氯化物配制金属离子总浓度为0.01～0.5mol/L的金属离子溶液，其中三氯化铁与二价金属氯化物的质量比为2∶1，将氢氧化钠或氨水加入到蒸馏水中配制浓度为0.5～5mol/L的碱溶液，将硫代硫酸钠、硼氢化钠或水合肼加入到蒸馏水中配制浓度为0.2～2mol/L的水溶性还原剂溶液；二、将金属离子溶液、碱溶液和水溶性还...
【技术保护点】
1.一种磁性纳米线的制备方法，其特征在于磁性纳米线的制备方法，按以下步骤进行：一、用蒸馏水、三氯化铁和二价金属氯化物配制金属离子总浓度为0.01～0.5mol/L的金属离子溶液，其中三氯化铁与二价金属氯化物的质量比为2∶1，将氢氧化钠或氨水加入到蒸馏水中配制浓度为0.5～5mol/L的碱溶液，将硫代硫酸钠、硼氢化钠或水合肼加入到蒸馏水中配制浓度为0.2～2mol/L的水溶性还原剂溶液；二、将金属离子溶液、碱溶液和水溶性还原剂溶液进行混合，将混合溶液装入密封反应釜，然后置于磁场热处理炉中反应2～10h，磁场强度为0.1～0.4T，反应温度为120～200℃，得反应产物；三、将...
【技术特征摘要】
1.一种磁性纳米线的制备方法，其特征在于磁性纳米线的制备方法，按以下步骤进行：一、用蒸馏水、三氯化铁和二价金属氯化物配制金属离子总浓度为0.01～0.5mol/L的金属离子溶液，其中三氯化铁与二价金属氯化物的质量比为2∶1，将氢氧化钠或氨水加入到蒸馏水中配制浓度为0.5～5mol/L的碱溶液，将硫代硫酸钠、硼氢化钠或水合肼加入到蒸馏水中配制浓度为0.2～2mol/L的水溶性还原剂溶液；二、将金属离子溶液、碱溶液和水溶性还原剂溶液进行混合，将混合溶液装入密封反应釜，然后置于磁场热处理炉中反应2～10h，磁场强度为0.1～0.4T，反应温度为120～200...
【专利技术属性】
技术研发人员：黄勇，
申请(专利权)人：鄄城永铭地毯有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。