一种磁性碳纳米球的制备方法技术

本发明专利技术公开了一种磁性碳纳米球的制备方法，是以萘或1,5‑二羟基萘为碳源，三嵌段共聚物PF127为表面活性剂，在铁源二茂铁存在下，于含有双氧水的无水乙醇溶剂体系中进行溶剂热反应，一步法制备磁性碳纳米球。本发明专利技术方法成本低廉，反应温度较低，反应时间短，制备的磁性碳纳米球纯度高，化学稳定性好，可应用于吸附材料、催化剂载体、药物中间体等技术领域，实用性广。

Preparation of magnetic carbon nanospheres

The invention discloses a preparation method of magnetic carbon nanospheres. The magnetic carbon nanospheres are prepared by solvent thermal reaction in anhydrous ethanol solvent system containing hydrogen peroxide in the presence of ferrocene with naphthalene or 1,5 -dihydroxy naphthalene as carbon source and triblock copolymer PF127 as surfactant. The method has the advantages of low cost, low reaction temperature, short reaction time, high purity and good chemical stability, and can be applied in the technical fields of adsorption materials, catalyst carriers, drug intermediates, etc., with wide practicability.

【技术实现步骤摘要】
一种磁性碳纳米球的制备方法
本专利技术涉及一种碳纳米球的制备方法，特别是一种磁性碳纳米球的制备方法。本专利技术采用溶剂热法制备所述磁性碳纳米球。
技术介绍
Fe3O4是一种优良的磁性纳米粒子，在外加磁场作用下，能够实现便捷的定位、分离等。然而，由于磁性纳米粒子的粒径小，比表面能大，以及粒子之间存在的磁偶极相互作用，非常容易发生团聚和沉降，很大程度上限制了其应用。为了解决上述问题，常常会通过其他材料来包覆磁性纳米粒子。与其他材料相比，碳纳米材料表现出更高的化学稳定性、热力学稳定性及生物相容性等。碳纳米球凭借其低密度、稳定的物理化学性质和优异的导电性等优势，广泛用作电极材料、储氢材料、吸附材料等。将碳纳米球与Fe3O4复合制备的磁性微球在废水处理、油品脱硫等领域效果显著。目前制备磁性碳纳米球的方法主要包括电弧放电法、化学气相沉积法、热解法、溶剂热法等。但是，这些方法一般都需要较高的温度、复杂的制备路线和较长的反应时间，因此能耗较大，在一定程度上限制了其应用。Johnson等[ChemCommun,2004,2442-2443]以硬脂酸铁为原料，在氩气气氛下900℃一步热解生成碳包覆铁的F本文档来自技高网...

【技术保护点】
1.一种磁性碳纳米球的制备方法，是以萘或1,5‑二羟基萘为碳源，三嵌段共聚物PF127为表面活性剂，在铁源二茂铁存在下，于含有双氧水的无水乙醇溶剂体系中进行溶剂热反应，以制备所述磁性碳纳米球。

【技术特征摘要】
1.一种磁性碳纳米球的制备方法，是以萘或1,5-二羟基萘为碳源，三嵌段共聚物PF127为表面活性剂，在铁源二茂铁存在下，于含有双氧水的无水乙醇溶剂体系中进行溶剂热反应，以制备所述磁性碳纳米球。2.根据权利要求1所述的磁性碳纳米球的制备方法，其特征是所述铁源二茂铁的用量为碳源质量的2～3倍。3.根据权利要求1所述的磁性碳纳米球的制备方法，其特征是所述PF127的用量是碳源质量的3～5倍。4.根据权利要求1所述的磁性碳纳米球的制备方法，其特征是...

【专利技术属性】
技术研发人员：刘旭光，崔燕，康伟伟，秦蕾，杨永珍，
申请(专利权)人：太原理工大学，
类型：发明
国别省市：山西,14