The present invention relates to a lithium-ion battery electrode sheet. During the coating process, the active substances adhered to the cathode slurry are separated by the thickness of the active substance. After drying and winding, the electrode sheet with high porosity and low voidage interval can be obtained by pressing in a continuous rolling mill. The wavy size is: the thickness size is A, the thin size is B, (A_B)/B=10_30%, the thickness interval C, C=3_6 mm. After rolling, the thickness becomes uniform, and the number of particles in the coating varies regularly with high and low voidage intervals. When the battery is charged and discharged, the conduction rate of lithium ion is greatly increased due to the existence of low voidage particles. Thus, the high rate charge-discharge performance of lithium battery can be greatly improved without decreasing the energy density. \u3002
【技术实现步骤摘要】
一种锂离子电池极片
本专利技术涉及锂离子电池领域，具体涉及一种锂离子电池极片。
技术介绍
目前锂离子电池的正负极极片均按照单一的厚度进行覆料，在极片烘干后进行碾压的过程中，尤其在较大的压力下容易使极片出现过压情况，具体表现在极片内部空隙率过低，从而导致出现烘烤后极卷绕时出现极片断裂，电解液浸润变差等异常，使制作的锂电池大电流充放电性能及安全性降低。
技术实现思路
本专利技术提供一种锂离子电池极片的设计方法，通过提供一种内部颗粒间空隙率按照一定规律变化的极片，可以在不降低锂电池能量密度的情况下不仅能够避免锂离子极片在碾压时出现过压从而导致极片变脆易折断的问题，且能够大大加快极片在注液时的吸液速度，提升注液效率，同时能够提升极片在电解液中的浸润效果，提升电池的放电倍率性能。为了实现以上效果，本专利技术采用以下的极片设计：一种锂离子电池极片,其特征在于：在极片的涂布过程中，涂布正极浆料附着在集流体上的活性物质厚薄互相间隔的波浪型涂层，再经烘干收卷，通过连轧机进压薄，即可以得到内部高孔隙率和低空隙率间隔出现的极片。进一步地，所述波浪型尺寸：厚处尺寸为A，薄处尺寸为B，(A-B...
【技术保护点】
1.一种锂离子电池极片,其特征在于：在极片的涂布过程中，涂布正极浆料附着在集流体上的活性物质厚薄互相间隔的波浪型，再经烘干收卷，通过连轧机进压薄，即可以得到内部高孔隙率和低空隙率间隔出现的极片；所述波浪型尺寸：厚处尺寸为A，薄处尺寸为B，(A‑B)/B=10‑30%,厚薄间隔C，C=3‑6mm。
【技术特征摘要】
1.一种锂离子电池极片,其特征在于：在极片的涂布过程中，涂布正极浆料附着在集流体上的活性物质厚薄互相间隔的波浪型，再经烘干收卷，通过连轧机进压薄，即...
【专利技术属性】
技术研发人员：宋泽斌，杨清欣，吴支红，杨晓旭，张兴，
申请(专利权)人：长虹三杰新能源有限公司，
类型：发明
国别省市：江苏,32