The invention discloses a solar water heater heat absorbent and a production method. The solar water heater heat absorbent is prepared from the following raw material components and weight proportion: carbon powder 20 30, zinc powder 2 8, titanium dioxide 15 25, aluminium silicate 10 15, calcium chloride 7 14, polyethylene dilute alcohol 3 8, calcium carbonate 5 10, sodium silicate 5 10. After mixing according to the weight of each component, according to the material 5 10, water 90 95, dilution and stirring uniformly, solar water heater heat absorbing material is made. The invention has high heat absorption rate and ideal heat absorption effect for sunlight. Durable, long service life, can increase service life by more than 30%. It is widely used and easy to popularize.
【技术实现步骤摘要】
太阳能热水器吸热剂及生产方法
本专利技术涉及一种吸热材料，特别是一种太阳能热水器的吸热材料。
技术介绍
目前，太阳能热水器的吸热材料，采用了无光漆等，这些材料虽然成本低、操作简单，但对太阳光的吸热效果不是很理想，吸热率不是很高，直接影响到太阳能热水器的推广应用。
技术实现思路
本专利技术目的在于克服现有技术的不足，提供一种吸热率高、使用寿命长的太阳能热水器吸热剂。本专利技术由下列原料组份和重量比例配制而成：碳粉20-30、锌粉2-8、钛白粉15-25、硅酸铝10-15、氯化钙7-14、聚乙稀醇3-8、碳酸钙5-10、硅酸钠5-10。本专利技术太阳能热水器吸热剂的生产方法如下：按各组份重量备料混合后，按备料5-10；水90-95，稀释搅拌均匀，制成太阳能热水器吸热材料。生产太阳能热水器时，将太阳能热水器吸热材料涂刷在太阳能热水器的集热板或集热管上，阴干或烤干即可。与现有技术相比，本专利技术具有如下优点：1、吸热率高，对太阳光的吸热效果理想。2、经久耐用，使用寿命长，可提高使用寿命30％以上。3、使用本产品绿色环保，无污染4、使用面广，容易推广。具体实施方式实施例1，太阳能热水器吸热剂按以下成分和重量比进行备料：碳粉25、锌粉5、钛白粉20、硅酸铝12、氯化钙12、聚乙稀醇7、碳酸钙10、硅酸钠9。按各组份重量备料混合后，按备料8％，水92％，稀释搅拌均匀，制成太阳能热水器吸热剂。实施例2，太阳能热水器吸热剂按以下成分和重量比进行备料：碳粉20、锌粉8、钛白粉25、硅酸铝10、氯化钙10、聚乙稀醇8、碳酸钙9、硅酸钠10。按各组份重量备料混合后，按备料5％，水95...
【技术保护点】
1.太阳能热水器吸热剂，其特征在于：由下列原料组份和重量比例配制而成：碳粉20‑30、锌粉2‑8、钛白粉15‑25、硅酸铝10‑15、氯化钙7‑14、聚乙稀醇3‑8、碳酸钙5‑10、硅酸钠5‑10。
【技术特征摘要】
1.太阳能热水器吸热剂，其特征在于：由下列原料组份和重量比例配制而成：碳粉20-30、锌粉2-8、钛白粉15-25、硅酸铝10-15、氯化钙7-14、聚乙稀醇3-8、碳酸钙5-10、...
【专利技术属性】
技术研发人员：魏铨举，魏志明，
申请(专利权)人：四川锦明新能源科技有限公司，
类型：发明
国别省市：四川,51