一种电暖器用防腐涂料的制备方法技术

本发明专利技术公开了一种电暖器用防腐涂料的制备方法，包括以下具体步骤：在容器内放入二乙烷、滑石粉和氯化钠，升高容器温度，搅拌10‑20分钟后，加入少量水，持续搅拌；再加入十六烷基苯磺酸钠、聚乙烯醇和甲酸，升高容器温度为70‑85摄氏度，继续搅拌；持续反应25‑35分钟后，保持温度不变，继续搅拌，缓慢滴加盐酸，搅拌至稠状，得到防腐涂料。

A preparation method of anticorrosive coating for electric heater

The invention discloses a preparation method of an anticorrosive coating for electric heater, which comprises the following specific steps: adding diethylene, talc powder and sodium chloride into the container, raising the temperature of the container, stirring for 10 to 20 minutes, adding a small amount of water, and continuously stirring; adding sodium Hexadecylbenzene sulfonate, polyvinyl alcohol and formic acid, raising the temperature of the container to 70 to 85 degrees Celsius, and continuing stirring; After 25 35 minutes of reaction, keep the temperature unchanged, continue to stir, slowly add hydrochloric acid, stir until thick, get anticorrosive coating.

【技术实现步骤摘要】
一种电暖器用防腐涂料的制备方法
本专利技术属于电暖器
，具体涉及一种电暖器用防腐涂料的制备方法。
技术介绍
电暖器，可广泛用于住宅、办公室、宾馆、商场、医院、学校、火车车厢等移动供暖、简易活动房等各类民用与公共建筑。集辐射与对流于一身，内部为高效能铝合金散热翼板，辐射能力强、辐射面积大，采用电热膜为发热材料，它超大面积的黑晶镜面外观时尚，完全满足了讲究居室装饰美观人群的苛刻要求。
技术实现思路
为解决现有技术的不足，本专利技术的目的在于提供一种方法简单，工作效率高的电暖器用防腐涂料的制备方法。为了实现上述目标，本专利技术采用如下的技术方案：一种电暖器用防腐涂料的制备方法，包括以下具体步骤：在容器内放入二乙烷、滑石粉和氯化钠，升高容器温度，搅拌10-20分钟后，加入少量水，持续搅拌；再加入十六烷基苯磺酸钠、聚乙烯醇和甲酸，升高容器温度为70-85摄氏度，继续搅拌；持续反应25-35分钟后，保持温度不变，继续搅拌，缓慢滴加盐酸，搅拌至稠状，得到防腐涂料。优选的，升高容器温度为50-60摄氏度。优选的，搅拌速度为500-600转/min。本专利技术的有益之处在于：本专利技术的电暖器用防腐本文档来自技高网...

【技术保护点】
1.一种电暖器用防腐涂料的制备方法，其特征在于，包括以下具体步骤：在容器内放入二乙烷、滑石粉和氯化钠，升高容器温度，搅拌10‑20分钟后，加入少量水，持续搅拌；再加入十六烷基苯磺酸钠、聚乙烯醇和甲酸，升高容器温度为70‑85摄氏度，继续搅拌；持续反应25‑35分钟后，保持温度不变，继续搅拌，缓慢滴加盐酸，搅拌至稠状，得到防腐涂料。

【技术特征摘要】
1.一种电暖器用防腐涂料的制备方法，其特征在于，包括以下具体步骤：在容器内放入二乙烷、滑石粉和氯化钠，升高容器温度，搅拌10-20分钟后，加入少量水，持续搅拌；再加入十六烷基苯磺酸钠、聚乙烯醇和甲酸，升高容器温度为70-85摄氏度，继续搅拌；持续反应25-35分钟后，保持...

【专利技术属性】
技术研发人员：耿帅，
申请(专利权)人：徐州星耀新能源科技有限公司，
类型：发明
国别省市：江苏,32