The invention belongs to the field of micro-nano material preparation technology, and provides a preparation method of hollow octahedral cuprous oxide, which comprises the following steps: (1) precipitation reaction is carried out after mixing copper chloride solution and sodium hydroxide solution to obtain precipitation solution; (2) reaction is carried out after mixing the precipitation solution, glucose and ammonia water to produce hollow octahedral cuprous oxide. The invention first uses sodium hydroxide and copper chloride to react to form copper hydroxide precipitation, then uses glucose to reduce copper ions, and uses ammonia water to produce graded diffusion dissolution effect on octahedral particles, resulting in gradual dissolution of octahedral particles into hollow structure. The results of the embodiments show that the method provided by the invention can prepare hollow octahedral cuprous oxide with uniform structure and purity.
【技术实现步骤摘要】
一种空心八面体氧化亚铜的制备方法
本专利技术涉及微纳材料制备
，尤其涉及一种空心八面体氧化亚铜的制备方法。
技术介绍
氧化亚铜是一种典型的p型半导体，禁带宽度为2～2.2ev，其具有良好的光电性能而应用于各个领域。例如利用氧化亚铜纳米线做为光电阴极裂解水产氢；氧化亚铜50面体作为一氧化碳催化生氢的氧化催化剂。近几年，空心结构形貌引起越来越广泛的关注，其特殊的表面结构、较大的比表面积、较好的稳定性等特点，在能源、催化、药物载体、气体传感等方面有着越来越重要的应用前景。目前关于空心结构形貌的合成方法主要有金属有机框架模板合成、酸刻蚀、碱刻蚀、气相刻蚀和高温热分解等方法。但是上述方法制备过程较为繁琐，需要多步处理，且能耗高，易污染环境。
技术实现思路
本专利技术的目的在于提供一种空心八面体氧化亚铜的制备方法，该方法成本低、能耗低、环境友好、操作简单，具有重要的学术意义和应用价值。为了实现上述专利技术目的，本专利技术提供以下技术方案：本专利技术提供了一种空心八面体氧化亚铜的制备方法，包含如下步骤：(1)将氯化铜溶液和氢氧化钠溶液混合后进行沉淀反应，得到沉淀液；(2)将所...
【技术保护点】
1.一种空心八面体氧化亚铜的制备方法，包含如下步骤：(1)将氯化铜溶液和氢氧化钠溶液混合后进行沉淀反应，得到沉淀液；(2)将所述沉淀液、葡萄糖和氨水混合后进行反应，生成空心八面体氧化亚铜。
【技术特征摘要】
1.一种空心八面体氧化亚铜的制备方法，包含如下步骤：(1)将氯化铜溶液和氢氧化钠溶液混合后进行沉淀反应，得到沉淀液；(2)将所述沉淀液、葡萄糖和氨水混合后进行反应，生成空心八面体氧化亚铜。2.根据权利要求1所述的制备方法，其特征在于，所述步骤(1)中沉淀反应的温度为15～30℃。3.根据权利要求1或2所述的制备方法，其特征在于，所述步骤(1)中氯化铜溶液的浓度为20～25g/L。4.根据权利要求1或2所述的制备方法，其特征在于，所述步骤(1)中氢氧化钠溶液的浓度为0.5～1.5mol/L。5.根据权利要求1或2所述的制备方法，其特征在于，所述步骤(1)中氯化铜溶液和氢氧化钠溶...
【专利技术属性】
技术研发人员：耿旺昌，赵叶军，何小伟，段利兵，张秋禹，
申请(专利权)人：西北工业大学，
类型：发明
国别省市：陕西,61