陶瓷核燃料芯块制造法制造技术

本发明专利技术涉及核动力技术，特别是以生产燃料元件为氧化物核燃料技术并可用于制造基于二氧化铀芯块的核燃料用于核电站。本发明专利技术的本质:一种制造二氧化铀核燃料芯块的方法，包括制备含或不含三氧化二铁铀的二氧化铀压塑粉，同时,二氧化铀粉比例为О/U＝2,37±0,04，作为原料制备压塑粉,使用已知的方法制备，即陶瓷级二氧化铀粉在空气中加热，比例为О/U＝2,01‑2,15.本发明专利技术的技术成果为提高烧结芯块的机械强度，增加烧结芯块的晶粒尺寸。

Manufacturing of Ceramic Nuclear Fuel Pellets

The present invention relates to nuclear power technology, in particular to the production of fuel elements as oxidized nuclear fuel technology and can be used to produce nuclear fuel based on uranium dioxide pellets for nuclear power plants. The essence of the invention is: a method for manufacturing uranium dioxide nuclear fuel pellets, including preparation of uranium dioxide compression powder containing or without uranium ferric oxide, at the same time, the ratio of uranium dioxide powder is /U=2,37+0,04, which is used as raw material to prepare compression powder and is prepared by known method, i.e. ceramics grade uranium dioxide powder is heated in air with the ratio of /U=2,01,2,15. In order to improve the mechanical strength of sintered pellets and increase the grain size of sintered pellets.

【技术实现步骤摘要】
【国外来华专利技术】陶瓷核燃料芯块制造法本专利技术属于核动力
，即核电站内燃料元件使用的二氧化铀陶瓷核燃料芯块制造工艺。由于对(U)铀–(O)氧复杂系统进行了(但尚未完成)长期研究，已确定存在超过20种氧化铀及其变形[马约罗夫阿.阿.,布拉韦尔曼伊.布.二氧化铀陶瓷粉末制造工艺俄联邦部长会议原子能利用委员会出版社1985年第10页2.1号图]，其中4个用于通过粉末冶金工艺制造陶瓷核燃料芯块：比如，目前已有包括压型二氧化铀粉末(UO2)的准备、其与润滑剂的混合、压制成芯块及还原性气氛下二氧化铀坯块的烧结这些工序的芯块制造方法(从1971年3月16日的1371595号英国专利特许证，МКИG21C3/62)。还有一个芯块制造方法[从1987年12月16日的0249549号EP专利特许证，МКИG21C3/62]，按照它为了获得烧结块而采用三氧化二铀U3O8粉末(三氧化二铀)与二氧化铀UO2粉末的混合物，且该混合物中的三氧化二铀U3O8为主。按照这一种方法获得的烧结块具有较低的密度和高孔率，这是由于三氧化二铀在烧结过程很早以前就在还原反应中发生微观结构变形并产生具有更高理论密度的最终产品(二氧化铀)而引起本文档来自技高网...

【技术保护点】
1.包括加不加有三氧化二铀粉末的二氧化铀压塑粉的制备，压塑粉的压制及还原气氛下进行的压型芯块烧结这三个工序的核燃料芯块制造法，其特征在于，通过陶瓷级二氧化铀粉末在空气中进行加热而获得的U/O比例为2.37±0.4的二氧化铀粉末作为用料来制造压塑粉。

【技术特征摘要】
【国外来华专利技术】2017.05.12 RU 20171165131.包括加不加有三氧化二铀粉末的二氧化铀压塑粉的制备，压塑粉的压制及还原气氛...

【专利技术属性】
技术研发人员：V·V·希洛夫，
申请(专利权)人：化工科学研究院股份公司，科学与创新股份公司，
类型：发明
国别省市：俄罗斯,RU