The invention discloses a preparation method of large sample electrolytic sample of bearing steel, which first takes rough sample on bearing steel, then anneals the rough sample by spheroidizing, then polishes or polishes the rough sample, and then obtains the sample; the spheroidizing annealing process is: heating the rough sample to 790-810 (?) with the furnace heating, holding for 3-6 hours, then cooling to 650 (?) and below, taking out the air-cooled sample. \u3002 After spheroidizing annealing, the sample structure changes from lamellar pearlite to spherical pearlite, which effectively prevents the lamellar metal from falling off during the electrolysis process. In the electrolysis process, the large sample of bearing steel prepared by this method can effectively prevent the lamellar metal from falling off on the sample surface, improve the accuracy of the experimental results and reduce the labor intensity.
【技术实现步骤摘要】
轴承钢大样电解试样的制备方法
本专利技术涉及一种检测试样的制备方法，尤其是一种轴承钢大样电解试样的制备方法。
技术介绍
轴承素有“高端装备的关节”之称，是最重要的关键基础件之一。轴承主要的失效形式为接触疲劳失效和磨损失效，其中接触疲劳失效占主要地位。轴承在负荷工作时，轴承钢中的夹杂物会成为应力集中的裂纹源，是造成疲劳失效的主因。夹杂物极为有害，因此研究轴承钢中夹杂物的行为非常迫切和重要。大样电解法是评价钢中大型夹杂物非常有效的方法，也是目前为止无法替代的大型夹杂物分析方法之一，主要用于分析钢中大于50μm的夹杂物。大样电解法的电解机理是阳极：铁失去电子变成铁离子Fe-2e=Fe2+，阴极：铁离子得到电子变成铁Fe2++2e=Fe。在对轴承钢试样进行电解的过程中，不断会有片层状的金属从电解试样表面脱落，这严重影响了实验结果的准确性，同时增加了工作强度。这是因为轴承钢的轧后组织主要为片层状珠光体，片层状珠光体是渗碳体（Fe3C）和铁素体（α-Fe）组成的片层相间的组织，在电解过程中铁素体（α-Fe）易腐蚀，铁素体完全溶解后，试样表面的渗碳体及未被完全腐蚀的铁素体会呈片...
【技术保护点】
1.一种轴承钢大样电解试样的制备方法，其特征在于：先在轴承钢钢材上取粗样，然后对粗样进行球化退火，再将粗样车光或抛光，即可得到所述的试样；所述球化退火过程为：粗样随炉升温加热至790～810℃，保温3～6小时，然后随炉冷却至650℃及以下，取出空冷。
【技术特征摘要】
1.一种轴承钢大样电解试样的制备方法，其特征在于：先在轴承钢钢材上取粗样，然后对粗样进行球化退火，再将粗样车光或抛光，即可得到所述的试样；所述球化退火过程为：粗样随炉升温加热至790～810℃，保温3～6小时，然后随炉冷却至650℃及...
【专利技术属性】
技术研发人员：周丹，靖振权，巩彦坤，丁剑，高福彬，何璞，史进强，
申请(专利权)人：邯郸钢铁集团有限责任公司，河钢股份有限公司邯郸分公司，
类型：发明
国别省市：河北,13