本发明专利技术公开了一种复合型冷轧钢带用稳定剂，其特征在于，按重量计由以下原料配制而成：磷酸氢二钠1.3‑1.5份，丙二酸7.4‑10份，N‑甲基吡咯烷酮1.3‑1.5份，脂肪醇聚氧乙烯醚2.6‑3.0份，2‑氨乙基十七烯基咪唑啉1.5‑2.0份，仲烷基硫酸酯钠0.7‑1.5份，去离子水30‑40份。本发明专利技术的复合型冷轧钢带用稳定剂耐腐蚀性强，表面稳定性好，耐磨擦、耐热耐寒，成本低，节能，环保无污染且制备简单，使生产效率大大提升。

A Stabilizer for Composite Cold Rolled Steel Strip

The invention discloses a composite stabilizer for cold-rolled steel strip. The stabilizer is characterized in that the stabilizer is prepared by weight from the following raw materials: 1.3 1.5 phr of sodium hydrogen phosphate, 7.4 10 phr of malonic acid, 1.3 1.5 phr of N_methyl pyrrolidone, 2.6 3.0 phr of fatty alcohol polyoxyethylene ether, 1.5 2.0 phr of 2_aminoethyl heptadienyl imidazoline, 0.7 1.5 phr of sodium secondary alkyl sulfate, deionized water. Forty copies. The composite stabilizer for cold rolled steel strip has strong corrosion resistance, good surface stability, abrasion resistance, heat resistance and cold resistance, low cost, energy saving, environmental protection, pollution-free and simple preparation, and greatly improves production efficiency.

【技术实现步骤摘要】
一种复合型冷轧钢带用稳定剂
本专利技术涉及一种复合型冷轧钢带用稳定剂。
技术介绍
冷轧钢具有良好的性能，即通过冷轧，可以得到厚度更薄、精度更高的冷轧带钢和钢板，平直度高、表面光洁度高、冷轧钢表面清洁光亮、易于进行涂镀加工、品种多，用途广，同时具有冲压性能高和不时效、屈服点低的特点，所以冷轧钢具广泛的用途。但冷轧钢容易受腐蚀和表面稳定性差，往往耗能大，成本高，对环境也造成很大的污染。以上就成了冷轧钢带行业亟待解决的问题。
技术实现思路
本专利技术要解决上述问题提供一种耐腐蚀性强，表面稳定性好，耐磨擦、耐热、耐寒，成本低，且节能，环保的复合型冷轧钢带用稳定剂。为实现上述技术目的，本申请采用如下技术方案：一种复合型冷轧钢带用稳定剂，其特征在于，按重量计由以下原料配制而成：磷酸氢二钠1.3-1.5份，丙二酸7.4-10份，N-甲基吡咯烷酮1.3-1.5份，脂肪醇聚氧乙烯醚2.6-3.0份，2-氨乙基十七烯基咪唑啉1.5-2.0份，仲烷基硫酸酯钠0.7-1.5份，去离子水30-40份。如上所述的一种复合型冷轧钢带用稳定剂，其特征在于，按重量计由以下原料配制而成：磷酸氢二钠1.4份，丙二酸8份，N-本文档来自技高网...

【技术保护点】
1.一种复合型冷轧钢带用稳定剂，其特征在于，按重量计由以下原料配制而成：磷酸氢二钠1.3‑1.5份，丙二酸7.4‑10份，N‑甲基吡咯烷酮1.3‑1.5份，脂肪醇聚氧乙烯醚2.6‑3.0份，2‑氨乙基十七烯基咪唑啉1.5‑2.0份，仲烷基硫酸酯钠0.7‑1.5份，去离子水30‑40份。

【技术特征摘要】
1.一种复合型冷轧钢带用稳定剂，其特征在于，按重量计由以下原料配制而成：磷酸氢二钠1.3-1.5份，丙二酸7.4-10份，N-甲基吡咯烷酮1.3-1.5份，脂肪醇聚氧乙烯醚2.6-3.0份，2-氨乙基十七烯基咪唑啉1.5-2.0份，仲烷基硫酸酯钠0.7-1.5份，去离...