The invention discloses a production method of melamine modified glue for hot pressing, which is characterized by the following specific quality components: formaldehyde 50%, urea 40%, polyvinyl alcohol 2%, melamine 7% and starch 1%. The preparation method is as follows: a, formaldehyde 50% is pumped into the reaction kettle, PH is adjusted to 8.5, polyvinyl alcohol 7%, urea 8% is added to heat up; b, the temperature is raised to 88 (?) and the gas is stopped for 30 minutes. C, adjust PH value 4.8, polycondensation reaction 20 minutes; d, adjust PH value 5.0.5.2, add melamine 4%, reaction 10 minutes, add urea 8%; e, reaction 20 minutes, adjust PH value 8.0, add melamine 3%, urea 8%; f, reaction 20 minutes, reduce temperature, add urea 8%; g, temperature, add starch 1%, gelatinization 20 minutes; h, temperature, 65 degrees, add urea 8%; Discharge at 45 C.
【技术实现步骤摘要】
热压用三聚氰胺改性胶水的生产方法及产品
本专利技术涉及脲醛树脂生产
，尤其是一种热压用三聚氰胺改性胶水的生产方法及产品。
技术介绍
目前国内木料生产粘接主要以脲醛树脂胶为主，其工艺简单，成本较低、所以得到全面推广，但其甲醛释放量大，使用后的常常甲醛超标，但随着消费者环保意识的组建增强，国家环保政策的施行，生产相对较环保、甲醛释放量低的粘接胶，是企业发展的必由之路。
技术实现思路
本专利技术的目的在于为了克服现有技术的不足而提供一种成本较低、粘性好、甲醛释放量较低的热压用三聚氰胺改性胶水。其具体质量组份如下：甲醛50%尿素40%聚乙烯醇2%三聚氰胺7%淀粉1%其制备方法如下：a、甲醛50%抽入反应釜中，调节PH为8-8.5，加入聚乙烯醇7%、尿素8%升温；b、升温到88℃停气，保温30分钟；c、调节PH值4.8，缩聚反应20分钟；d、调节PH值5.0-5.2，加三聚氰胺4%，反应10分钟，加尿素8%；e、反应20分钟，调节PH值为8.0，加三聚氰胺3%、尿素8%；f、反应20分钟，降温，加尿素8%；g、温度降至80℃，加淀粉1%，糊化20分钟；h、温度降至65℃，...
【技术保护点】
1.热压用三聚氰胺改性胶水的生产方法，其特征在于：其具体质量组份如下：甲醛50%、尿素40%、聚乙烯醇2%、三聚氰胺7%、淀粉1%，其制备方法如下：（a）、甲醛50%抽入反应釜中，调节PH为8‑8.5，加入聚乙烯醇7%、尿素8%升温；（b）、升温到88℃停气，保温30分钟；（c）、调节PH值4.8，缩聚反应20分钟；（d）、调节PH值5.0‑5.2，加三聚氰胺4%，反应10分钟，加尿素8%；（e）、反应20分钟，调节PH值为8.0，加三聚氰胺3%、尿素8%；（f）、反应20分钟，降温，加尿素8%；（g）、温度降至80℃，加淀粉1%，糊化20分钟；（h）、温度降至65℃，加尿...
【技术特征摘要】
1.热压用三聚氰胺改性胶水的生产方法，其特征在于：其具体质量组份如下：甲醛50%、尿素40%、聚乙烯醇2%、三聚氰胺7%、淀粉1%，其制备方法如下：（a）、甲醛50%抽入反应釜中，调节PH为8-8.5，加入聚乙烯醇7%、尿素8%升温；（b）、升温到88℃停气，保温30分钟；（c）、调节PH值4.8，缩聚反应20分钟；（d）、调节PH值5.0-5.2...
【专利技术属性】
技术研发人员：何龙江，杨铁勋，何凤娟，何静，黄梓珈，贾伟君，
申请(专利权)人：南充市龙煌建材有限公司，
类型：发明
国别省市：四川,51