The invention discloses a silicon scale inhibitor and its preparation method and application. The silicon scale inhibitor is prepared by copolymerization of acrylic acid, 2 acrylamide, 2 methylpropionic acid and N tert-butyl acrylamide. The preparation process is simple, the production cost is low, and the silicon scale inhibitor has excellent scale inhibition effect. At the same time, the silicon scale inhibitor itself has no toxic and side effects on organisms, and is safe in use, and can meet the industrial cycle. The requirement of silicon scale inhibition in the field of water treatment for circular cooling is especially suitable for the inhibition of colloidal or silicate scale in circulating systems with high silicon content in raw water or circulating water.
【技术实现步骤摘要】
一种硅垢阻垢剂及制备方法和应用
本专利技术属于工业水处理领域，具体涉及一种硅垢阻垢剂及制备方法和应用。
技术介绍
硅是地球上含量最丰富的元素之一，也是水环境中最常见的胶体物质，在水中硅的溶解度通常在150～180mg·L-1之间。工业循环冷却水系统中，为降低补水量和排污量，循环水的浓缩倍率通常较高。但随着浓缩倍率的增加，高硅含量的水在运行过程中常常形成硅垢沉积于设备表面，导致设备传热效率降低及系统管路堵塞。硅垢一旦形成便很难去除，常采用具有强腐蚀性的NH4F·HF清洗形成的硅垢，但操作不当会造成危险。为了解决硅垢的沉积，人们常常采用加入阻垢剂的方法。美国专利US4711725公开了使用丙烯酸/2-丙烯酰胺-2-甲基丙磺酸/丙烯酸乙酯共聚物阻止水中磷酸钙垢的沉积，但并未对硅垢进行性能测试。中国专利CN106458670A公开了一种疏水改性的环氧烷氨基甲酸酯共聚物并用于阻止水中二氧化硅的沉积。中国专利CN106458671A公开了使用包含胺封端的聚氧化烯阻止水中二氧化硅的沉积。中国专利CN100545212C公开了使用己二酸/端氨基聚醚/二乙烯三胺共聚物和聚天冬氨酸钠...
【技术保护点】
1.一种硅垢阻垢剂，其特征在于，由共聚单体共聚而成，所述的共聚单体为丙烯酸、2‑丙烯酰胺‑2‑甲基丙磺酸和N‑叔丁基丙烯酰胺；所述的丙烯酸、2‑丙烯酰胺‑2‑甲基丙磺酸和N‑叔丁基丙烯酰胺的重量比为70~130:0~60:10~60。
【技术特征摘要】
1.一种硅垢阻垢剂，其特征在于，由共聚单体共聚而成，所述的共聚单体为丙烯酸、2-丙烯酰胺-2-甲基丙磺酸和N-叔丁基丙烯酰胺；所述的丙烯酸、2-丙烯酰胺-2-甲基丙磺酸和N-叔丁基丙烯酰胺的重量比为70~130:0~60:10~60。2.根据权利要求1所述的硅垢阻垢剂，其特征在于，所述的丙烯酸、2-丙烯酰胺-2-甲基丙磺酸和N-叔丁基丙烯酰胺的重量比为120~130:50~60:15~60。3.根据权利要求1所述的硅垢阻垢剂，其特征在于，所述的丙烯酸和N-叔丁基丙烯酰胺的重量比为70~90:10~30。4.根据权利要求1所述的硅垢阻垢剂，其特征在于，所述硅垢阻垢剂的粘均分子量为4500~5500，分子量分布系数为3.0~4.0。5.一种权利要求1所述的硅垢阻垢剂的制备方法，其特征在于，将丙烯酸、2-丙烯酰胺-2-甲基...
【专利技术属性】
技术研发人员：高灿柱，邱同同，杜淑娟，蔡少康，程终发，赵开源，王宁宁，
申请(专利权)人：山东大学，山东泰和水处理科技股份有限公司，
类型：发明