用超精细粉煤灰和矿渣生产加气混凝土的方法技术

本发明专利技术涉及用超精细粉煤灰和矿渣生产加气混凝土的方法，本发明专利技术公开了用超精细粉煤灰和矿渣生产加气混凝土的方法及其制备技术，以质量百分比计，原料的加入量为：超精细粉煤灰和矿渣：50‑70％；硅酸盐水泥：10‑20％；生石灰：5‑20％；二水石膏：5‑10％。本发明专利技术相对于现有技术，具有如下优势：(1)较大量地利用超精细粉煤灰和矿渣生产加气混凝土，属资源化利用技术，可大幅度降低其昂贵的处理费用。(2)充分利用了金属铝成分。

Method of producing aerated concrete with superfine fly ash and slag

The invention relates to a method for producing aerated concrete with ultra-fine fly ash and slag, and discloses a method for producing aerated concrete with ultra-fine fly ash and slag and its preparation technology. In terms of mass percentage, the amount of raw materials added is as follows: ultra-fine fly ash and slag: 50 70%; Portland cement: 10 20%; quicklime: 5 20%; dihydrate gypsum: 5 10%; \u3002 Compared with the existing technology, the invention has the following advantages: (1) It is a resource utilization technology to produce aerated concrete by using a large number of ultra-fine fly ash and slag, and can greatly reduce its expensive treatment cost. (2) Making full use of the composition of metal aluminium.

【技术实现步骤摘要】
用超精细粉煤灰和矿渣生产加气混凝土的方法
本专利技术涉及一种复合材料，特别涉及用超精细粉煤灰和矿渣生产加气混凝土的方法及其制备技术。
技术介绍
随着我国经济的快速发展，发电厂、城市供热工程不断增加，超精细粉煤灰和矿渣的产量也随之增多。2006年，我国仅火电厂就产生约2.4～2.9亿吨超精细粉煤灰和矿渣和0.2～0.3亿吨炉渣，居世界之首。目前，西方发达国家的超精细粉煤灰和矿渣利用率已达80％以上，而我国仅为30％～40％左右。未获利用的超精细粉煤灰和矿渣大部分被排入贮灰厂、填埋场或江河湖海中。超精细粉煤灰和矿渣的堆积不仅占用大量土地，而且还会给周围环境造成严重污染，破坏生态平衡。因此，加大对超精细粉煤灰和矿渣综合利用的研究和开发显得日益重要。目前，超精细粉煤灰和矿渣主要资源化利用途径有：1)应用于水泥及混凝土中；2)用于建材制品生产；3)用于道路工程；4)应用于农业；5)应用于环境保护方面，作为污水处理、烟气脱硫和噪声防治介质；6)应用于化工领域，提取高纯明矾用以合成矾土、制备超精细粉煤灰和矿渣高分子填充材料、提取工业原料Al、Ge、Ga、Ag、Cd、U等多种金属元素。然而，在超精细本文档来自技高网...

【技术保护点】
1.用超精细粉煤灰和矿渣生产加气混凝土的方法。

【技术特征摘要】
1.用超精细粉煤灰和矿渣生产加气混凝土的方法。2.根据权利要求1所述的方法，其特征是，以质量百分比计，原料的加入量为：超精细粉煤灰和矿渣：50-70％；硅酸盐水泥：10-20％；生石灰：5-20％；二水石膏：5-10％。3.根据权利要求2所述的方法，其特征是，控制总水料比为0.5-0.8。4.根据权利要求2所述的方法，其特征是，拌合用水为70℃温水。5.根据权利要求2所述的方法，其特征是，具体步骤如下，(1)将超精细粉煤灰和矿渣加水做成料浆，搅拌(优选3-4分钟)；(2)加入硅酸盐水泥，搅拌(优选3-4分钟)；(3)加入二水石膏，搅拌(优选2-3分钟)；(4)加入生石灰，搅拌(优选2-3分钟)；抽至浇注车浆料搅拌罐中，开启...

【专利技术属性】
技术研发人员：杨媛，
申请(专利权)人：遵义景程环保材料有限公司，
类型：发明
国别省市：贵州,52