本发明专利技术的不锈钢工件的清洗方法，依次包括以下步骤：抛光工序，将不锈钢工件进行抛光处理；煮洗工序，该不锈钢工件在柴油、煤油或酒精的清洗液中煮洗并搅拌；超声清洗工序，该不锈钢工件被依次置于丙酮溶剂和异丙酮溶剂中进行超声波清洗；退火处理；以及退磁处理。该清洗方法可高效去除不锈钢工件的油渍、毛刺、氧化皮、焊渣等杂质，以保证良好清洗效果。

Cleaning Method of Stainless Steel Workpiece

The cleaning method of the stainless steel workpiece comprises the following steps in turn: polishing process, polishing the stainless steel workpiece; boiling and stirring process, in which the stainless steel workpiece is boiled and stirred in the cleaning liquid of diesel oil, kerosene or alcohol; ultrasonic cleaning process, in which the stainless steel workpiece is sequentially placed in acetone solvent and isoacetone solvent for ultrasonic cleaning; annealing process; And demagnetization treatment. The cleaning method can effectively remove oil stains, burrs, oxide scales, welding slag and other impurities of stainless steel workpieces to ensure a good cleaning effect.

【技术实现步骤摘要】
不锈钢工件的清洗方法
本专利技术涉及不锈钢工件清洗领域，尤其涉及一种不锈钢工件的清洗方法。
技术介绍
不锈钢工件的传统清洗方法十分粗糙，通常使用去离子水进行清洗，继而进行人工抛光，从而保证不锈钢工件的使用性能。但是这种清洗效果十分有限，尤其是对于复杂结构的不锈钢工件，此种清洗方法无法保证每个部位都能清洗干净。有些改进型的清洗方法是在化学清洗液中进行浸泡处理，使得不锈钢工件的清洗效果稍有提高。然而，清洗效果仍不尽如人意。故此，亟需一种改进的不锈钢工件的清洗方法，以克服以上的缺陷。
技术实现思路
本专利技术的目的在于提供一种不锈钢工件的清洗方法，其采用超声波清洗以及化学清洗相结合，高效去除不锈钢工件的油渍、毛刺、氧化皮、焊渣等杂质，以保证良好清洗效果。为实现上述目的，本专利技术的不锈钢工件的清洗方法，依次包括以下步骤：抛光工序，将不锈钢工件进行抛光处理；煮洗工序，该不锈钢工件在柴油、煤油或酒精的清洗液中煮洗并搅拌；超声清洗工序，该不锈钢工件被依次置于丙酮溶剂和异丙酮溶剂中进行超声波清洗；退火处理；以及退磁处理。与现有技术相比，本专利技术的不锈钢工件的清洗方法依次对不锈钢工件进行抛光、煮洗、超本文档来自技高网...

【技术保护点】
1.一种不锈钢工件的清洗方法，依次包括以下步骤：抛光工序，将不锈钢工件进行抛光处理；煮洗工序，该不锈钢工件在柴油、煤油或酒精的清洗液中煮洗并搅拌；超声清洗工序，该不锈钢工件被依次置于丙酮溶剂和异丙酮溶剂中进行超声波清洗；退火处理；以及退磁处理。

【技术特征摘要】
1.一种不锈钢工件的清洗方法，依次包括以下步骤：抛光工序，将不锈钢工件进行抛光处理；煮洗工序，该不锈钢工件在柴油、煤油或酒精的清洗液中煮洗并搅拌；超声清洗工序，该不锈钢工件被依次置于丙酮溶剂和异丙酮溶剂中进行超声波清洗；退火处理；以及退磁处理。2.如权利要求1所述的不锈钢工件的清洗方法，其特征在于：在所述煮洗工序之后、所述超声清洗工序之前，还包括：采用去离子水对该不锈钢工件进行喷淋处理。3.如权利要求1所述的不锈钢工件的清洗方法，其特征在于：在所述退磁处理之后，还包括：对该不锈钢工件进行清水漂洗及烘干处理。4.如权利要求1所述的不锈钢工件的清洗方法，其特征在于：所述抛光工序具体包括：用金属抛光液或砂纸打磨对所述不锈钢工件进行抛光处理，继而采用有机溶剂擦拭所述不锈钢工件。5.如权利要求1所述的...