The invention belongs to the field of building materials, and puts forward a composition of the main material of asphalt pavement material. The raw materials include 50 60 parts of petroleum asphalt, 15 25 parts of phenolic resin, 10 15 parts of EVA resin adhesive, 1 5 parts of propylene glycol methyl ether acetate, 1 5 parts of urea, 1 3 parts of aliphatic amine and 1 3 parts of activated carbon powder. The wear resistance and compression resistance of the products are better than those of ordinary asphalt materials. It has stable performance, good weather resistance, high temperature resistance and not easy to volatilize toxic and harmful gases, simple process and reasonable cost, and can be popularized and applied.
【技术实现步骤摘要】
一种沥青路面材料主料成分组成
本专利技术属于建筑材料领域,具体涉及一种沥青路面材料主料成分组成。
技术介绍
筑路常用的有机结合料,要求具有良好的技术性能,夏天不软化,冬天不发脆,能抵抗水、冰、盐类的侵蚀和行车的破坏作用并能有效降低路面的轮胎噪音。沥青材料是一种性价比十分高的选择。随着汽车工业的不断进步,对沥青路面材料的耐磨性及抗压性提出了更高的要求。
技术实现思路
本专利技术的目的在于提高路面沥青材料的耐磨性及抗压性,提出一种沥青路面材料主料成分组成。技术方案为实现上述专利技术目的,本专利技术提供了以下技术方案:一种沥青路面材料主料成分组成,原料按重量份包括:石油沥青50-60份,酚醛树脂15-25份,EVA树脂胶10-15份,丙二醇甲醚醋酸酯1-5份,尿素1-5份,脂肪胺1-3份,活性炭粉末1-3份。本专利技术的有益作用在于:1.制成产品的耐磨性及抗压性优于普通沥青材料。2.性能稳定,耐候性好,耐高温不易挥发有毒有害气体。3.工艺简单,成本合理,可推广应用。具体实施方式为了使本专利技术实现的技术手段、创作特征、达成目的与功效易于明白易懂,下面结合具体实施例对本专利技术进一步详细说明,但本专利技术的内容完全不局限于此。实施例1一种沥青路面材料主料成分组成,原料按重量包括:石油沥青50Kg,酚醛树脂16Kg,EVA树脂胶12Kg,丙二醇甲醚醋酸酯3Kg,尿素2Kg,脂肪胺1Kg,活性炭粉末1Kg。实施例2一种沥青路面材料主料成分组成,原料按重量包括:石油沥青55Kg,酚醛树脂22Kg,EVA树脂胶13Kg,丙二醇甲醚醋酸酯3Kg,尿素2Kg,脂肪胺2Kg,活性炭 ...
【技术保护点】
1.一种沥青路面材料主料成分组成,其特征在于,原料按重量份包括:石油沥青50‑60份,酚醛树脂15‑25份,EVA树脂胶10‑15份,丙二醇甲醚醋酸酯1‑5份,尿素1‑5份,脂肪胺1‑3份,活性炭粉末1‑3份。
【技术特征摘要】
1.一种沥青路面材料主料成分组成,其特征在于,原料按重量份包括:石油沥青50-60份,酚醛树脂15-25...