The invention relates to a polyether ether ketone composite material, which comprises the following components by weight: polyether ether ketone 40-90 copies, polyphenyl ester 10-20 copies, para-polyphenyl 5-15 copies, short glass fiber 5-40 copies, molybdenum disulfide 0.5-5 copies, graphene 0.5-5 copies, coupling agent 0.1-5 copies, antioxidant 0.2-0.5 copies. The invention has the following characteristics: the thermal conductivity of PEEK composite material is obviously improved, and obvious progress is made in the aspects of tensile strength, spherical pressure hardness, friction coefficient and linear expansion coefficient. In particular, some of the properties have been significantly improved, and some additives can reduce costs. Some special products with this material can fully meet the very harsh industrial, automotive, aerospace and military applications.
【技术实现步骤摘要】
一种聚醚醚酮复合材料
本专利技术涉及一种工程树脂,更确切地说是涉及一种聚醚醚酮复合材料。
技术介绍
芳香聚合物聚醚醚酮(PEEK)树脂是近年来综合性能优良的一种耐高温、耐化学试剂和刚韧性优异的热塑性工程塑料,如英国Victrex公司和国内的吉林大学等单位生产,随着热塑性树脂基复合材料成型技术的发展,采用PEEK树脂与其他材料共混的复合材料替代金属的耐磨材料,如衬套、齿轮、轴承、阀座等,在国内外已有多种产品问世,应用也趋于广泛。但单一组分的聚醚醚酮在性能上不够好,性能还有待于提高。以聚醚醚酮为基进行复合的材料有了一些技术文件的公开,如与聚四氟乙烯基材料复合;一般用于提高强度并降低磨擦系数,而聚醚醚酮为基在其它方面也极有潜力可以挖掘。
技术实现思路
本专利技术目的是:提出一种新型聚醚醚酮复合材料及其制备方法,尤其是提高材料的导热系数和提高对热变形温度的耐受性,用于提高材料的综合性能。本专利技术的目的还在于提出复合材料配方和制备方法,同时有助于提高材料强度并降低磨擦系数。本专利技术的具体技术方案如下:一种聚醚醚酮复合材料,按照重量份数计包括如下组份:聚醚醚酮40~90份,聚苯酯10~20份,对位聚苯5~15份、短玻璃纤维5~40份,二硫化钼0.5~5份,石墨烯0.5~5份,偶联剂0.1~5份,抗氧剂0.2~0.5份。优选的,所述的聚醚醚酮复合材料按照重量份数计包括如下组份:聚醚醚酮60~70份,聚苯酯14~16份,对位聚苯8~12份、短玻璃纤维15~30份,二硫化钼2~4份,石墨烯2~3份,偶联剂1~3份,抗氧剂0.2~0.5份。优选的,所述的聚醚醚酮复合材料按照重 ...
【技术保护点】
1.一种聚醚醚酮复合材料,其特征在于按照重量份数计包括如下组份:聚醚醚酮40~90份,聚苯酯10~20份,对位聚苯5~15份、短玻璃纤维5~40份,二硫化钼0.5~5份,石墨烯0.5~5份,偶联剂0.1~5份,抗氧剂0.2~0.5份。
【技术特征摘要】
1.一种聚醚醚酮复合材料,其特征在于按照重量份数计包括如下组份:聚醚醚酮40~90份,聚苯酯10~20份,对位聚苯5~15份、短玻璃纤维5~40份,二硫化钼0.5~5份,石墨烯0.5~5份,偶联剂0.1~5份,抗氧剂0.2~0.5份。2.根据权利要求1所述的聚醚醚酮复合材料,其特征在于按照重量份数计包括如下组份:聚醚醚酮60~70份,聚苯酯14~16份,对位聚苯8~12份、...