Composition of elastic polyether ether ketone modified material and its preparation method

The invention relates to a flexible polyether ether ketone modified material composition, which comprises the following components in weight: polyether ether ketone: 69-84 parts; silicone rubber: 10-30 parts; zinc stearate coupling agent: 0.5-5 parts. The invention has the following beneficial effects: 1) Compared with the unmodified PEEK material, the material has good elasticity and creep resistance; can be used in the sealing field to make the sealing effect better; can also be used in the cable industry of nuclear power plant; 2) the material obtained by the invention has wear resistance; 3) the material obtained by the invention has good chemical resistance.

【技术实现步骤摘要】
具有弹性的聚醚醚酮改性材料组合物及其制备方法
本专利技术涉及一种具有弹性的聚醚醚酮改性材料组合物及其制备方法，属于特种新材料领域。
技术介绍
聚醚醚酮(PEEK)树脂本身具有耐高温、耐磨损、耐化学性能好和机械强度好等综合性能优良等特点，广泛应用于各行各业。但是由于PEEK纯树脂加工后的零件硬度比较高或者没有韧性；限制了其部分应用，如何在保证材料的耐高温、耐磨损以及耐化学性能优良的不大幅下降前提下，让PEEK树脂通过改性具有一定的弹性，可以进一步拓宽其在密封行业以及线缆行业的应用。
技术实现思路
针对现有技术中的缺陷，本专利技术的目的是提供一种具有弹性的聚醚醚酮改性材料组合物及其制备方法。本专利技术是通过以下技术方案实现的：一种具有弹性的聚醚醚酮改性材料组合物，其包括按重量份数计的如下组分：聚醚醚酮：69～84份；硅橡胶：10～30份；硬脂酸锌偶联剂：0.5～5份。作为优选方案，所述硅橡胶的粒径为10～100μm。作为优选方案，所述硬脂酸锌偶联剂的粒径为40～50μm。一种如前述的具有弹性的聚醚醚酮改性材料组合物的制备方法，其包括如下步骤：将聚醚醚酮、硅橡胶和硬脂酸锌偶联剂混匀后，得到混合本文档来自技高网...

【技术保护点】
1.一种具有弹性的聚醚醚酮改性材料组合物，其特征在于，包括按重量份数计的如下组分：聚醚醚酮：            69～84份；硅橡胶：              10～30份；硬脂酸锌偶联剂：      0.5～5份。

【技术特征摘要】
1.一种具有弹性的聚醚醚酮改性材料组合物，其特征在于，包括按重量份数计的如下组分：聚醚醚酮：69～84份；硅橡胶：10～30份；硬脂酸锌偶联剂：0.5～5份。2.如权利要求1所述的具有弹性的聚醚醚酮改性材料组合物，其特征在于，所述硅橡胶的粒径为10～100μm。3.如权利要求1所述的具有弹性的聚醚醚酮改性材料组合物，其特征在于，所述硬脂酸锌偶联剂的粒径为40～50μm。4.一种如权利要求1所述的具有弹性的聚醚醚酮改性材料组合物的制备方法，其特征在于，包括...

【专利技术属性】
技术研发人员：顾伟，杨帆，
申请(专利权)人：南通汇平高分子新材料有限公司，
类型：发明
国别省市：江苏,32