The invention belongs to the field of building materials, and puts forward a composition of composite insulation board slurry. The raw materials include: 30 40 parts of prefabricated concrete construction waste with particle size not exceeding 200 purposes, 10 20 parts of ordinary Portland cement, 15 25 parts of expanded perlite particles, 10 20 parts of building gypsum, 10 20 parts of epoxy resin, 1 3 parts of sodium methyl silicate, 1 3 parts of diaminodiphenylmethane, 1 3 parts of building gypsum, 1 Polybutadiene rubber 1 5 parts; overcome the shortcomings of common insulation board, which is not fire-resistant and flammable, and the burning performance of the product reaches at least B1 level; the production cost is low, and the environmental pollution is small.
【技术实现步骤摘要】
一种复合保温板浆料组成
本专利技术属于建筑材料领域，具体涉及一种复合保温板浆料组成。
技术介绍
随着城市建设步伐的加快，城市大拆大建，许多七八十年代的预制房屋拆除之后产生大量建筑废料。这些建筑废料大多为水泥制品，难降解，如处理不当，易造成大规模环境污染。这些废旧建筑预制构件废料，经过高温煅烧，形成稳定、多孔、轻质的微观结构，若经特殊工艺处理，能够获得价值很高的耐火原料。利用这些废旧建筑预制构件废料不仅节约了国家的矿物资源和能源，而且也减少了环境污染，降低材料的成本。
技术实现思路
本专利技术的目的在于减少环境污染，降低保温板制作成本，提出一种复合保温板浆料组成。技术方案为实现上述专利技术目的，本专利技术提供了以下技术方案：一种复合保温板浆料组成，原料按重量份包括：粒径不超过200目的预制混凝土构建废料30-40份，普通硅酸盐水泥10-20份，膨胀珍珠岩颗粒15-25份，建筑石膏10-20份，环氧树脂10-20份，甲基硅醇钠1-3份，二氨基二苯基甲烷1-3份，聚丁二烯橡胶1-5份。本专利技术的有益作用在于：1.克服了普通保温板不耐火易燃的缺点，制成产品燃烧性能至少达到B1级。2.保温效果好，有效切断热桥，保温隔热。3.利用废旧原料，制作成本低，环境污染小。具体实施方式为了使本专利技术实现的技术手段、创作特征、达成目的与功效易于明白易懂，下面结合具体实施例对本专利技术进一步详细说明，但本专利技术的内容完全不局限于此。实施例1一种复合保温板浆料组成，原料按重量份包括：粒径不超过200目的预制混凝土构建废料30Kg，普通硅酸盐水泥10Kg，膨胀珍珠岩颗粒15Kg，建筑...
【技术保护点】
1.一种复合保温板浆料组成，其特征在于，原料按重量份包括：粒径不超过200目的预制混凝土构建废料30‑40份，普通硅酸盐水泥10‑20份，膨胀珍珠岩颗粒15‑25份，建筑石膏10‑20份，环氧树脂10‑20份，甲基硅醇钠1‑3份， 二氨基二苯基甲烷1‑3份，聚丁二烯橡胶1‑5份。
【技术特征摘要】
1.一种复合保温板浆料组成，其特征在于，原料按重量份包括：粒径不超过200目的预制混凝土构建废料30-40份，普通硅酸盐水泥10-20份，...