一种湿法转化制硫酸催化剂的制备方法技术

一种湿法转化制硫酸催化剂的制备方法，属于催化剂技术领域。其特征是将含有钠和钾离子的钒水溶液经过与硫酸中和后得到胶体沉淀，该胶体沉淀与硅藻土加水碾合后挤条、烘干，烘干样浸渍酸性溶液后再烘干、焙烧，最后制得湿法转化制硫酸催化剂。该催化剂在湿法转化催化制硫酸过程中具有良好的活性和稳定性，可用于湿法转化制硫酸转化器的任何部分使用。

Preparation of a Catalyst for Wet Conversion to Sulfuric Acid

The invention relates to a preparation method of a catalyst for wet conversion to sulphuric acid, belonging to the technical field of catalyst. It is characterized by colloidal precipitation of vanadium aqueous solution containing sodium and potassium ions after neutralization with sulphuric acid. The colloidal precipitation is rolled with diatomite by adding water, then extruded and dried. The dried sample is impregnated with acid solution, then dried and roasted. Finally, a catalyst for wet conversion of sulphuric acid is prepared. The catalyst has good activity and stability in the process of wet conversion catalytic sulfuric acid production, and can be used in any part of the converter of wet conversion sulfuric acid production.

【技术实现步骤摘要】
一种湿法转化制硫酸催化剂的制备方法
本专利技术涉及一种湿法转化制硫酸催化剂的制备方法，属于催化剂制备

技术介绍
钒催化剂被广泛使用于硫酸生产装置，主要将二氧化硫转化为三氧化硫。传统的钒催化剂主要用于干法制硫酸装置，即二氧化硫在催化转化过程中没有水蒸气存在。而硫酸湿法转化工艺的特点是原料气中含有大量的水蒸气，二氧化硫的催化转化生成三氧化硫后直接与水蒸气形成硫酸。显而易见，湿接触法制酸是无需洗涤、干燥，在水蒸汽存在下将二氧化硫催化转化成三氧化硫，并直接凝结成酸，制酸工艺更简单，更有利于系统能量的回收利用，大大降低了投资和生产成本。湿法制酸催化剂是湿法制酸工艺的核心技术，由于工艺不同，传统的干法催化剂应用在湿法装置上，存在强度下降，转化率降低，使用寿命短等问题。为了解决上述问题，本专利提出了一种湿法转化制硫酸催化剂的制备方法。
技术实现思路
本专利技术的目的是提出一种湿法转化制硫酸催化剂的制备方法，降低酸性改性剂的用量。本专利技术的特点是突破传统工艺在挤条过程中引入酸性溶液改性剂，创造性地采用将挤条、烘干后的烘干样浸渍酸性改性剂溶液的工艺。本专利技术一种湿法转化制硫酸催化剂的制备方法本文档来自技高网...

【技术保护点】
1.一种湿法转化制硫酸催化剂的制备方法，其特征在于，将含有钠和钾离子的钒水溶液经过与硫酸中和后得到胶体沉淀，该胶体沉淀与硅藻土加水碾合后挤条、烘干，烘干样浸渍酸性改性剂溶液后再烘干、焙烧，最后制得湿法转化制硫酸催化剂。

【技术特征摘要】
1.一种湿法转化制硫酸催化剂的制备方法，其特征在于，将含有钠和钾离子的钒水溶液经过与硫酸中和后得到胶体沉淀，该胶体沉淀与硅藻土加水碾合后挤条、烘干，烘干样浸渍酸性改性剂溶液后再烘干、焙烧，最后制得湿法转化制硫酸催化剂。2.根据权利要求1所述的湿法转化制硫酸催化剂的制备方法，其特征在于，钒水溶液中金属元素以氧化物形式的质量比为：K2O/V2O5=2.5-3.5，Na2O/V2O5=0.1-0.5。3.根据权利要求1所述的湿法转化制硫酸催化剂的制备方法，其特征在于，硅藻土为山东临朐硅藻土。4.根据权利要求1或3所述的湿法转化制硫酸催化...

【专利技术属性】
技术研发人员：贺健，田先国，谢天明，董天雷，殷惠琴，
申请(专利权)人：中国石油化工股份有限公司，南化集团研究院，
类型：发明
国别省市：江苏,32