The invention provides a fiber reinforced forming material, which takes vinyl ester (A), unsaturated monomer (B), polyisocyanate (C), polymerization initiator (D), and carbon fiber (E) with a fiber length of 2.5mm-50mm as essential raw materials. The vinyl ester (A) is a reactant of epoxy resin (a1) and (methyl) acrylic acid (a2) with an epoxy equivalent of 180-500 ranges, in which the ethyl ester (C), the initiator (D) and the carbon fiber length of 2.5mm-50mm are used as necessary raw materials. The mass ratio of vinyl ester (A) to unsaturated monomer (B) ranges from 40/60 to 85/15, and the molar ratio of isocyanate group (NCO) of polyisocyanate (C) to hydroxyl group (OH) of vinyl ester (A) ranges from 0.25 to 0.85. The fibre reinforced forming material can be used for automobile components due to its excellent operating environment, processing and formability, appearance and bending strength.
【技术实现步骤摘要】
【国外来华专利技术】纤维增强成形材料和使用其的成形品
本专利技术涉及可获得成形材料的处理时的操作性、操作环境及成形性优异、弯曲强度、弯曲模量等各种物性优异的成形品的纤维增强成形材料及其成形品。
技术介绍
将碳纤维作为增强纤维来增强环氧树脂、不饱和聚酯树脂等热固化性树脂的纤维增强树脂复合材料的轻质且耐热性、机械强度优异的特征受到关注，以汽车或航空机的壳体或各种构件为代表，在各种结构体用途中的利用正在扩大。在该纤维增强树脂复合材料中，作为使用环氧树脂的材料的成形方法，已知有将称为预浸料的材料在可进行加压的高压釜中加热并使其固化的高压釜法，作为使用不饱和聚酯树脂的材料的成形方法，已知有使用称为片状模塑料(SMC)、块状模塑料(BMC)的中间材料来通过压制成形、注射成形等方法使其固化、成形的方法。特别是近年来，积极地进行生产性优异的材料开发。作为这种成形材料，已知有例如包含不饱和聚酯、乙烯基单体、热塑性聚合物、多异氰酸酯、填充材料、导电性炭黑及宽碳纤维束作为必需成分的碳纤维增强片状成形材料(例如，参照专利文献1。)。由该成形材料虽然可获得外观优异的成形品，但由于使用了挥发性高的苯乙烯单体，因...
【技术保护点】
1.一种纤维增强成形材料，其特征在于，以乙烯基酯A、闪点为100℃以上的不饱和单体B、多异氰酸酯C、聚合引发剂D、及纤维长2.5mm～50mm的碳纤维E作为必需原料，所述乙烯基酯A为环氧当量为180～500范围的环氧树脂a1和(甲基)丙烯酸a2的反应物，其中，所述乙烯基酯A与所述不饱和单体B的质量比即A/B为40/60～85/15的范围，所述多异氰酸酯C的异氰酸酯基NCO与所述乙烯基酯A的羟基OH的摩尔比即NCO/OH为0.25～0.85的范围。
【技术特征摘要】
【国外来华专利技术】2016.10.11 JP 2016-2001241.一种纤维增强成形材料，其特征在于，以乙烯基酯A、闪点为100℃以上的不饱和单体B、多异氰酸酯C、聚合引发剂D、及纤维长2.5mm～50mm的碳纤维E作为必需原料，所述乙烯基酯A为环氧当量为180～500范围的环氧树脂a1和(甲基)丙烯酸a2的反应物，其中，所述乙烯基酯A与所述不饱和单体B的质量比即A/B为40/60～85/15的范围，所述多异氰酸酯C的异氰酸酯基NCO与所述乙烯基酯A的羟基...
【专利技术属性】
技术研发人员：藤田幸子，安村隆志，
申请(专利权)人：DIC株式会社，
类型：发明
国别省市：日本,JP