The invention is a production process of high gloss and wear-resistant paper. The surface base paper is unwrapped by uncoiler, sprayed with pre-wetting glue, immersed in the impregnating glue after 5 to 10 minutes, then extruded by measuring roll, and then the paper passes through 2 to 3 m/min low speed flat roll, enters the oven, adopts multi-section oven drying process, after 5 to 8 hours of drying, the paper is cut. After cutting, the paper is stacked and turned with a stacker, and packed into storage. The pressing time is shorter, and the general pressing time is reduced by 5 seconds, which improves the production efficiency.
【技术实现步骤摘要】
一种高光耐磨纸生产工艺
本专利技术涉及特种用纸的生产方法，具体地说，是一种高光耐磨纸生产工艺。
技术介绍
耐磨纸广泛的用在橱柜、衣柜、贝尔强化复合地板的贴面中，贴面的纸张经过三聚氰胺胶水和一些添加剂浸渍后，和板材（密度板、刨花板、胶合板），经过热压机钢板的热压成为饰面板材；耐磨纸根据原纸功能的不同而不同，如果要达到装饰的效果，那么要用花色纸；如果要起到耐磨的效果，那么要用耐磨纸；如果要起到力学平衡的效果，那么要用平衡纸。市场上现有的耐磨纸存在以下几个缺陷：一是表面光泽度低，一般只有20Gs，强行提高钢板光泽度来使用，则表面光泽不均；二是花纹的纹理真实感不强。
技术实现思路
本专利技术的目的是旨在克服现有技术的不足之处而提出一种集装饰和耐磨于一体的高光耐磨纸及其生产工艺，按照本专利技术提出的技术方案所生产加工的高光耐磨纸用作强化板或其他装饰板表层材料，既具有极高的耐磨性能又富有极佳的高清晰装饰美感效果，可以取代装饰纸和耐磨纸，具有极好的镜面，模压，浮雕，亚光效果。本专利技术披露的一种高光耐磨纸生产工艺，将表层原纸，通过开卷机放卷，喷涂配置好的预湿胶水后，静放5-10min后浸入配好浸渍胶水，再通过计量辊挤去多余的胶水，然后纸张经过2-3m/min的低转速度整平辊，进入烘箱，采用多节烘箱烘干工艺，经过5-8h烘干后，将裁切后的纸张，用翻垛机整垛翻面，包装入库。本专利技术的进一步改进，所述预湿胶水和所述浸渍胶水采用三聚氰胺聚甲醛树脂，在PH9-10碱性条件下，通过温度80-95控制胶水缩合反应速度，2小时的缩合反应，延长到3小时，增加胶水均匀性，胶水平均粘度由15....
【技术保护点】
1.一种高光耐磨纸生产工艺，其特征在于，将表层原纸，通过开卷机放卷，喷涂配置好的预湿胶水后，静放5‑10min后浸入配好浸渍胶水，再通过计量辊挤去多余的胶水，然后纸张经过2‑3m/min的低转速度整平辊，进入烘箱，采用多节烘箱烘干工艺，经过5‑8h烘干后，将裁切后的纸张，用翻垛机整垛翻面，包装入库。
【技术特征摘要】
1.一种高光耐磨纸生产工艺，其特征在于，将表层原纸，通过开卷机放卷，喷涂配置好的预湿胶水后，静放5-10min后浸入配好浸渍胶水，再通过计量辊挤去多余的胶水，然后纸张经过2-3m/min的低转速度整平辊，进入烘箱，采用多节烘箱烘干工艺，经过5-8h烘干后，将裁切后的纸张，用翻垛机整垛翻面，包装入库。2.根据权利要求1所述的高光耐磨纸生产工艺，其特征在于：所述预湿胶水和所述浸渍胶水采用三聚...