一种防静电涂层液制造技术

本发明专利技术涉及防静电技术领域，具体是一种防静电涂层液，该涂层液包括如下重量配比的原料：中性硅溶胶10‑20％，阴离子表面活性剂20‑30％，两性表面活性剂0.1‑1％，其余为水。该产品新颖独特，将涂层液应用于RC相纸的背面，具有较强的防静电能力，且防电涂层防水性和附着力强，不易脱落，解决了RC相纸的生产制造、运输和使用中因静电造成的产品损害，以及机械力造成的防电涂层脱落等问题。

An Antistatic Coating Solution

The invention relates to the field of anti-static technology, in particular to an anti-static coating liquid, which comprises raw materials of the following weight ratio: neutral silica sol 10_20%, anionic surfactant 20_30%, amphoteric surfactant 0.1_1%, and the rest is water. The product is novel and unique. The coating solution is applied on the back of RC phase paper. It has strong anti-static ability. The anti-static coating has strong waterproof and adhesion, and is not easy to fall off. It solves the problems of product damage caused by static electricity in the manufacture, transportation and use of RC phase paper, and the anti-static coating falling off caused by mechanical force.

【技术实现步骤摘要】
一种防静电涂层液
本专利技术涉及防静电涂层液，特别是涉及应用于RC相纸中的防静电涂层液。
技术介绍
感光材料使用的基材由于具有极端的疏水性，故此极易吸附静电荷，因此在涂布、干燥、裁切、运输以及后期使用过程中，常因摩擦而产生高压静电，形成静电斑。通常正电荷表现为静电斑点，负电荷表现为树枝状。随着照相乳剂感光度的提高、涂布车速的提高、环境湿度的降低，静电斑产生的几率增大，严重时造成大批产品报废，造成极大的损失。RC高光相纸是用双面涂塑淋膜相纸底纸经多层涂布后的相纸，RC高光相纸由于设备投入较大，涂布次数较多，工艺较复杂，成品率较低，因此避免因静电作用导致成品的损耗是目前亟待要解决的问题。目前常用的抗静电技术是采用抗静电剂，一般是将少量的抗静电剂添加到塑料内部或直接涂布到塑料产品表面，可有效抑制静电产生。抗静电剂按分子结构可分为表面活性剂类抗静电剂和高分子型抗静电剂两大类。目前常用的抗静电剂主要有阳离子抗静电剂、阴离子型抗静电剂、非离子型抗静电剂、两性抗静电剂、高分子型抗静电剂。而产品的表面电阻率为106-1012ohm/sq的抗静电能力最大，而如何在该范围内尽量降低表面电阻率是目前行业的本文档来自技高网...

【技术保护点】
1.一种防静电涂层液，其特征在于，包括如下重量配比的原料：中性硅溶胶10‑20％，阴离子表面活性剂20‑30％，两性表面活性剂0.1‑1％，其余为水。

【技术特征摘要】
1.一种防静电涂层液，其特征在于，包括如下重量配比的原料：中性硅溶胶10-20％，阴离子表面活性剂20-30％，两性表面活性剂0.1-1％，其余为水。2.根据权利要求1所述的防静电涂层液，其特征在于，所述中性硅溶胶中SiO2浓度为24-26％。3.根据权利要求2所述的防静电涂层液，其特征在于，所述中性硅溶胶中SiO2的平均粒径为10-15nm。4.根据权利要...