易燃低烟耐磨复合纱线制造技术

本发明专利技术公开了易燃低烟耐磨复合纱线，以重量计，所述易燃耐磨复合纱线的原材料包括：蚕丝10‑15、涤纶15‑20、粘胶纱20‑30、高强度聚乙烯短纤维40‑60和纳米微胶囊助燃剂0.5‑1，采用上述技术方案得出的易燃低烟耐磨复合纱线在燃烧时会使纺织品在遭遇火灾时快速的燃烧，从而减少产生的浓烟，减少了火灾中因为浓烟而造成的死亡几率，同时还增加了耐磨的性能，提高了家用的实用性。

Flammable low smoke wear resistant composite yarn

The invention discloses flammable low smoke and wear resistant composite yarn. The raw materials of the flammable and wear resistant composite yarn include silk 10 15, polyester 15 20, viscose yarn 20 30, high strength polyethylene staple fiber 40 60 and nano microcapsule combustible additive 0.5 1. The flammable and low smoke and wear resistant composite yarn obtained by the above technical scheme can cause textiles to encounter fire when burning. Fast burning, thus reducing the smoke generated, reducing the probability of death caused by smoke in the fire, but also increased the wear resistance, improve the practicability of household.

【技术实现步骤摘要】
易燃低烟耐磨复合纱线
本专利技术属于纺织领域，尤其涉及易燃低烟耐磨复合纱线。
技术介绍
复合纱线是指两种以上不同的纤维以单纱或长丝交缠在一起类似股线结构，可在改造后的细纱机上纺出，也可以在空心锭子纺出。传统的复合纱线都是将几种纤维简单的交缠在一起得到复合纱线，这样织出的复合纱线功能太过单一，不能满足现如今人们对纺织物的高标准以及高要求。
技术实现思路
专利技术目的：本专利技术旨在解决上述难题，提出易燃低烟耐磨复合纱线。技术方案：易燃低烟耐磨复合纱线，以重量计，所述易燃耐磨复合纱线的原材料包括：蚕丝10-15、涤纶15-20、粘胶纱20-30、高强度聚乙烯短纤维40-60和纳米微胶囊助燃剂0.5-1。进一步的，所述纳米微胶囊助燃剂包括纳米金属粉末、乙醇、苯乙烯、六水氯化铁和丙酮。进一步的，所述纳米微胶囊助燃剂制作方法为：(1)、将纳米金属粉末和乙醇混合并放入超声波发生器中，混合3-5min；(2)、依次加入苯乙烯和六水氯化铁，得到混合物；(3)、将混合物置入氮气环境下，升温至55-70℃，并在超声波发生器中持续搅拌24-48h；(4)、将混合物置入离心机中沉降；(5)、用丙酮洗涤混合物后，本文档来自技高网...

【技术保护点】
1.易燃低烟耐磨复合纱线，其特征在于，以重量计，所述易燃耐磨复合纱线的原材料包括：蚕丝10‑15、涤纶15‑20、粘胶纱20‑30、高强度聚乙烯短纤维40‑60和纳米微胶囊助燃剂0.5‑1。

【技术特征摘要】
1.易燃低烟耐磨复合纱线，其特征在于，以重量计，所述易燃耐磨复合纱线的原材料包括：蚕丝10-15、涤纶15-20、粘胶纱20-30、高强度聚乙烯短纤维40-60和纳米微胶囊助燃剂0.5-1。2.根据权利要求1所述的易燃低烟耐磨复合纱线，其特征在于：所述纳米微胶囊助燃剂包括纳米金属粉末、乙醇、苯乙烯、六水氯化铁和丙酮。3.根据权利要求2所述的易燃低烟耐磨复合纱线，其特征在于：所述纳米微胶囊助燃剂制作方法为：(1)、将纳米金属粉末和乙醇混合并放入超声波发生器中，混合3-5min；(2)、依次加入苯乙烯和六水氯化铁，得到混合物；(3)、将混合物置入氮气环境下，升温至55-70℃，并在超声波发生器中持续搅拌24-48h；(4)、将混合物置入离心机中沉...

【专利技术属性】
技术研发人员：赵宏华，
申请(专利权)人：扬州永辉纺织科技有限公司，
类型：发明
国别省市：江苏,32