The invention discloses a moisture absorption and moisture release heat shrinkable film, which comprises the following components: 100 parts of polyethylene, 1-3 parts of antioxidant, 2-4 parts of light stabilizer, 0.5-1 part of terephthalic dioctyl ester, 1-2 parts of magnesium stearate, 5-10 parts of flax fiber, 4-8 parts of bamboo fiber and 2-4 parts of cotton fiber, and the weight ratio of bamboo fiber to cotton fiber is 2:1. By mixing polyethylene, antioxidant, light stabilizer, di-octyl terephthalate, magnesium stearate and modified fibers, melting, extrusion and granulation, blowing and stretching, the hygroscopic and dehumidifying heat shrinkable film was obtained.
【技术实现步骤摘要】
一种吸湿放湿性热收缩膜及其制备方法
本专利技术涉及一种吸湿放湿性热收缩膜以及制备方法。
技术介绍
热收缩膜是一种具有良好的热收缩性的包装薄膜，热收缩膜因其优异的稳定性和安全性，在食品、药品、饮料等领域得到了广泛的应用，热收缩膜的种类繁多，有PE热收缩膜、PVC热收缩膜、POF热收缩膜、OPS热收缩膜等等；但是不管哪一种的热收缩膜，为了进一步拓宽热收缩膜在包装行业的应用范围，需要对热收缩膜的阻燃性以及耐高温性进行全面的提升。
技术实现思路
针对上述现有技术的不足之处，本专利技术解决的问题为：提供一种吸湿放湿性好并且不影响柔性、阻燃性好热收缩膜以及制备方法。为解决上述问题，本专利技术采取的技术方案如下：一种吸湿放湿性热收缩膜，包括以下重量份的组分：聚乙烯100份、抗氧化剂1～3份、光稳定剂2～4份、对苯二甲二辛酯0.5～1份、硬脂酸镁1～2份、亚麻纤维5～10份、竹纤维4～8份、棉纤维2～4份；所述的竹纤维和棉纤维的重量比为2：1。进一步，包括以下重量份的组分：聚乙烯100份、抗氧化剂2份、光稳定剂3份、对苯二甲二辛酯0.7份、硬脂酸镁1.5份、亚麻纤维7份、竹纤维6份、...
【技术保护点】
1.一种吸湿放湿性热收缩膜，其特征在于，包括以下重量份的组分：聚乙烯100份、抗氧化剂1～3份、光稳定剂2～4份、对苯二甲二辛酯0.5～1份、硬脂酸镁1～2份、亚麻纤维5～10份、竹纤维4～8份、棉纤维2～4份；所述的竹纤维和棉纤维的重量比为2：1。
【技术特征摘要】
1.一种吸湿放湿性热收缩膜，其特征在于，包括以下重量份的组分：聚乙烯100份、抗氧化剂1～3份、光稳定剂2～4份、对苯二甲二辛酯0.5～1份、硬脂酸镁1～2份、亚麻纤维5～10份、竹纤维4～8份、棉纤维2～4份；所述的竹纤维和棉纤维的重量比为2：1。2.根据权利要求1所述的吸湿放湿性热收缩膜，其特征在于，包括以下重量份的组分：聚乙烯100份、抗氧化剂2份、光稳定剂3份、对苯二甲二辛酯0.7份、硬脂酸镁1.5份、亚麻纤维7份、竹纤维6份、棉纤维3份。3.根据权利要求1所述的吸湿放湿性热收缩膜，其特征在于，所述的抗氧化剂为丁基羟基茴香醚、二丁基羟基甲苯、叔丁基对苯二酚中的一种或几种。4.根据权利要求1所述的吸湿放湿性热收缩膜，其特征在于，所述的光稳定剂为光稳定剂944。5.一种吸湿放湿性热收缩膜的制备方法，其特征在于，步骤如下：S1、将亚麻纤维送入研磨机中进行充分研磨，得到粉体状态的亚麻纤维，将粉态状的亚麻纤维中加入水，进行充分搅拌，得到亚麻纤维浆液；S2、将竹纤维送入研磨机中进行充分研磨，得...