The invention discloses a green environmental protection ceramic tile adhesive, which comprises the following components: 100-200 parts of mineral powder, 50-100 parts of nano-calcium carbonate powder, 100-150 parts of glutinous rice glue, 100-150 parts of carrageenan, 50-60 parts of latex, 200-400 parts of quartz sand, 1-5 parts of guar gum ether and 0-2 parts of starch ether. The invention can ensure that the ceramic tiles are firmly adhered, odorless and pollution-free, and will not cause harm to human body. Due to the addition of natural materials such as glutinous rice glue and carrageenan, there will be no release of harmful substances such as formaldehyde, and it has the characteristics of green environmental protection.
【技术实现步骤摘要】
一种绿色环保瓷砖胶
本专利技术涉及一种绿色环保瓷砖胶,属于建筑材料。
技术介绍
在家庭卫生间墙壁上基本都需要贴瓷砖,常见的方法是在瓷砖背面涂上一层瓷砖胶,再将瓷砖直接贴合在墙壁上,瓷砖胶干后即可将瓷砖固定在墙壁表面。目前采用的瓷砖胶中大多含有对人体有危害的成分比如甲醛,即使经过较长的时间也难以挥发,因此如何降低其中的有害物质是当前工作的一个亟待解决的问题。
技术实现思路
针对上述现有技术存在的问题,本专利技术的目的是提供一种在保证瓷砖牢固贴合的情况下能够降低挥发物对人体和环境产生危害的绿色环保瓷砖胶。为实现上述目的,本专利技术采用的技术方案是:一种绿色环保瓷砖胶,包括以下重量份的各组分:矿粉100~200份、纳米碳酸钙粉50~100份、糯米胶100~150份、卡拉胶100~150份、乳胶50~60份、石英砂200~400份、瓜尔胶醚1~5份、淀粉醚0~2份。优选的,包括以下重量份的各组分:矿粉100份、纳米碳酸钙粉100份、糯米胶100份、卡拉胶100份、乳胶60份、石英砂400份、瓜尔胶醚2.5份、淀粉醚1份。优选的,所述矿粉为S95级矿粉。优选的,所述纳米碳酸钙粉的粒径为10-15μm。作为最优选的方案,所述石英砂为50wt%的100~180目石英砂和50wt%的200-350目石英砂混合而成。本专利技术能够保证瓷砖牢固贴合,无异味且无污染,不会对人体产生危害,由于添加了糯米胶、卡拉胶等天然材料,不会有甲醛等有害物质释放,具有绿色环保的特性。具体实施方式下面结合实施例对本专利技术作进一步详细说明。实施例1本专利技术的绿色环保瓷砖胶包括以下重量份的各组分:矿 ...
【技术保护点】
1.一种绿色环保瓷砖胶,其特征在于,包括以下重量份的各组分:矿粉100~200份、纳米碳酸钙粉50~100份、糯米胶100~150份、卡拉胶100~150份、乳胶50~60份、石英砂200~400份、瓜尔胶醚1~5份、淀粉醚0~2份。
【技术特征摘要】
1.一种绿色环保瓷砖胶,其特征在于,包括以下重量份的各组分:矿粉100~200份、纳米碳酸钙粉50~100份、糯米胶100~150份、卡拉胶100~150份、乳胶50~60份、石英砂200~400份、瓜尔胶醚1~5份、淀粉醚0~2份。2.根据权利要求1所述的绿色环保瓷砖胶,其特征在于,包括以下重量份的各组分:矿粉100份、纳米碳酸钙粉100份、糯米胶100份、卡拉胶100...