The invention relates to a processing method for fish rod raw materials, which comprises the following steps: 1) putting polyimide, carbon fibers, polyethylene fibers, titanium alloy wires, aramid fibers and Teflon into a mixer and mixing them evenly at high temperature; 2) ultrasonic treatment of raw materials in the above steps for 15-20 minutes; 3) putting them into a reaction vessel and adding magnesium carbonate, calcium stearate and coumarin indene resin. Reaction, reaction at high temperature/45-55 minutes; 4) After the reaction mixture material in the twin-screw extruder extrusion granulation, that is to make fishing rod composite materials. The technical problem to be solved by the invention is to provide a processing method for fishing rod raw material, which is novel in technology and can produce carbon fiber fishing rod raw material with low cost, good toughness, light weight, good oxidation resistance and antistatic performance.
【技术实现步骤摘要】
一种鱼竿原料的加工方法
本专利技术涉及一种鱼竿原料的加工方法。
技术介绍
随着人们生活水平的不断提高，垂钓已经成为人们一种重要的娱乐、休闲活动，竞技钓鱼也如火如荼的频繁开展，目前市场上的鱼竿绝大部分是碳纤维钓竿，均是采用无梭纺碳纤维纵向布制管，经浸树脂固化而制造的，用于钓竿生产方面的碳纤维含量多少，直接决定钓竿的价值和品位，一般含碳量为30％、90％左右，用碳纤维制造的钓竿具有轻、坚实、抗拉强度高的特点，现有的制造鱼竿用材料虽然已经具有了优异的抗张强度、屈服强度和伸长率等机械性能，但是其抗静电性能、韧性和耐老化性能不高，在使用过程中还是具有限制诸多限制。
技术实现思路
本专利技术所要解决的技术问题在于提供一种鱼竿原料的加工方法，工艺新颖，可以制造出成本低，韧性好、质量轻、具有较好的抗氧化性能和抗静电性能的碳纤维鱼竿原料。本专利技术所要解决的技术问题采用以下的技术方案来实现：一种鱼竿原料的加工方法，步骤如下：1)将聚酰亚胺、碳纤维、聚乙烯纤维、钛合金丝、芳纶纤维、特氟龙投入混合机中，以上质量份数计的组分制备而成：聚酰亚胺60～85份，碳纤维35～50份，聚乙烯纤维30～...
【技术保护点】
1.一种鱼竿原料的加工方法，步骤如下：1)将聚酰亚胺、碳纤维、聚乙烯纤维、钛合金丝、芳纶纤维、特氟龙投入混合机中，以上质量份数计的组分制备而成：聚酰亚胺60～85份，碳纤维35～50份，聚乙烯纤维30～45份，钛合金丝15～30份，芳纶纤维8～15份，特氟龙9～20份；高温搅拌状态下混合均匀；2)将上述步骤中的原料超声15～20min；3)然后将其放入到反应容器中加入碳酸镁、硬脂酸钙、香豆酮茚树脂进行反应，以上质量份数计的组分制备而成：碳酸镁12～18份、硬脂酸钙10～25份、香豆酮茚树脂7～10份；高温下反应40～55分钟；4)将反应后的混合物料在双螺杆挤出机中挤出造粒，...
【技术特征摘要】
1.一种鱼竿原料的加工方法，步骤如下：1)将聚酰亚胺、碳纤维、聚乙烯纤维、钛合金丝、芳纶纤维、特氟龙投入混合机中，以上质量份数计的组分制备而成：聚酰亚胺60～85份，碳纤维35～50份，聚乙烯纤维30～45份，钛合金丝15～30份，芳纶纤维8～15份，特氟龙9～20份；高温搅拌状态下混合均匀；2)将上...