The present invention relates to a process for producing accelerator and aluminate flocculant for shotcrete with aluminium ash, waste acid and waste alkali. The technical core is to promote the reaction of alumina in aluminium ash with acid-alkali solution to soluble aluminium salt by using the contact exothermic characteristic of aluminium metal in aluminium ash and acid-alkali solution without external heating source. The process design is not only used for manufacturing accelerator and flocculant. The raw material selection is novel and creative, which provides a simple and value-added disposal method for a large number of industrial waste liquor treatment. After implementation, it has outstanding practicability, especially in the comprehensive treatment of energy saving, consumption reduction and waste liquor disposal of environmental pollution.
【技术实现步骤摘要】
利用铝灰制造速凝剂和絮凝剂的工艺方法所属
本专利技术涉及铝灰和废酸、废碱制造喷射混凝土用速凝剂(以下简称：速凝剂)和铝酸盐类用于污水净化的絮凝剂(以下简称：絮凝剂)系列产品的一种工艺方法，属于工业废弃物再生资源综合利用领域。
技术介绍
铝灰产生于铝冶炼熔渣二次加工后废弃物，主要成份为金属铝5～15％、氧化铝50～80％，并含有一定量的氮化铝，而氮化铝遇水分解生成氨气产生的恶臭味影响环境，目前提取金属铝后的铝灰不允许填埋大部分直接堆存，因此减少铝灰库存压力无害化的处理和铝资源综合利用技术研发具有广泛的社会效益。化工、农药、玻璃、钢铁、冶金、电子等企业生产中副产大量废酸、废碱液体，这些废液的清洁排放运行成本非常高，一般企业难以承受，因此亟需一种资源综合利用方法，对该行业的废酸、废碱液体进行合理有效处理。
技术实现思路
本专利技术提供一种利用铝灰和废酸、废碱液生产速凝剂和絮凝剂的工艺方法，其主要目的在于克服废酸、废碱液与铝灰混合反应中放热快，并有易燃氢气和恶臭味氨气清洁排放生产运行成本高和资源综合利用经济效益低的缺陷。为解决上述缺陷问题，本专利技术采用如下工艺方案：方案①、...
【技术保护点】
1.利用废渣废液制造速凝剂和絮凝剂的工艺方法，其特征在于，包括如下方案：方案①使用耐酸碱搅拌设备将铝灰与废酸液拌和成膏状混合料，经陈化、烘干、粉碎、装包工序制成粉剂产品。方案②使用耐酸碱搅拌设备将铝灰与废碱液和适量激发剂搅拌成糊状浆料，经浓缩、过滤制成铝酸钠溶液。方案③使用耐酸碱搅拌设备将铝灰与废碱液或副产碱渣和石灰石粉或电石渣等含钙类脱硅助剂搅拌成膏状或复配粉磨混合，经高温烧结制成铝酸钠熟料。
【技术特征摘要】
2018.11.29 CN 20182198482701.利用废渣废液制造速凝剂和絮凝剂的工艺方法，其特征在于，包括如下方案：方案①使用耐酸碱搅拌设备将铝灰与废酸液拌和成膏状混合料，经陈化、烘干、粉碎、装包工序制成粉剂产品。方案②使用耐酸碱搅拌设备将铝灰与废碱液和适量激发剂搅拌成糊状浆料，经浓缩、过滤制成铝酸钠溶液。方案③使用耐酸碱搅拌...