The embodiment of the invention relates to the technical field of coating, and discloses a material surface treatment method and a shell. In the present invention, the material surface treatment method includes: spraying the primer on the material to form a primer layer; among them, the color brightness of the material is lower than the preset threshold; NCVM coating is carried out on the material after spraying the primer to form a coating layer; the thickness of the coating layer is less than the preset threshold; and the first color of the coating layer is sprayed. The first color is the color of the material, and the color paste concentration of the first color is less than the preset concentration, which makes it not easy to drop the paint when using non-conductive electroplating technology NCVM to present a dark effect.
【技术实现步骤摘要】
素材表面处理方法和外壳
本专利技术实施例涉及镀膜
，特别涉及一种素材表面处理方法和外壳。
技术介绍
随着手机表面处理方法的发展，金属外壳越来越多，颜色也越来越丰富多样，铝合金氧化颜色越来越多，且黑色哑光或深色已渐成流行色。然而，专利技术人发现现有技术中至少存在如下问题：手机侧按键或摄像头装饰件多为塑胶材料，为整体颜色效果的一致，要求侧按键及摄相头装饰件也需要做到和阳化件一样的深色，通常采用不导电电镀技术NCVM，但做成深色时，容易出现掉漆的问题。
技术实现思路
本专利技术实施方式的目的在于提供一种素材表面处理方法和外壳，使得利用不导电电镀技术NCVM，呈现深色效果时，不容易出现掉漆的问题。为解决上述技术问题，本专利技术的实施方式提供了一种素材表面处理方法，包括：对所述素材喷涂底漆，形成底漆层；其中，所述素材的颜色的色彩明度低于预设门限；采用镀膜材料对经过喷涂底漆的所述素材进行NCVM镀膜，形成镀膜层；其中，所述镀膜层的厚度小于预设阈值；在所述镀膜层喷涂第一颜色的油漆，形成中漆层；其中，所述第一颜色为所述素材的颜色，所述第一颜色的油漆中的色浆浓度小于预设浓度。本专...
【技术保护点】
1.一种素材表面处理方法，其特征在于，包括：对所述素材喷涂底漆，形成底漆层；其中，所述素材的颜色的色彩明度低于预设门限；采用镀膜材料对经过喷涂底漆的所述素材进行NCVM镀膜，形成镀膜层；其中，所述镀膜层的厚度小于预设阈值；在所述镀膜层喷涂第一颜色的油漆，形成中漆层；其中，所述第一颜色为所述素材的颜色，所述第一颜色的油漆中的色浆浓度小于预设浓度。
【技术特征摘要】
1.一种素材表面处理方法，其特征在于，包括：对所述素材喷涂底漆，形成底漆层；其中，所述素材的颜色的色彩明度低于预设门限；采用镀膜材料对经过喷涂底漆的所述素材进行NCVM镀膜，形成镀膜层；其中，所述镀膜层的厚度小于预设阈值；在所述镀膜层喷涂第一颜色的油漆，形成中漆层；其中，所述第一颜色为所述素材的颜色，所述第一颜色的油漆中的色浆浓度小于预设浓度。2.根据权利要求1所述的素材表面处理方法，其特征在于，所述色彩明度与所述预设阈值对应，且所述色彩明度越低，所述预设阈值小。3.根据权利要求1所述的素材表面处理方法，其特征在于，所述预设阈值小于或等于1um。4.根据权利要求1所述的素材表面处理方法，其特征在于，所述镀膜层的厚度通过所述镀膜材料的重量控制；其中，所述镀膜材料的重量越轻，所述镀膜层的厚度越薄。5.根据权利要求4所...
【专利技术属性】
技术研发人员：丁兆荣，
申请(专利权)人：上海创功通讯技术有限公司，
类型：发明
国别省市：上海,31