The invention discloses a preparation method of a semi-coke loaded manganese-copper adsorbent for dry desulfurization and denitrification. The semi-coke is used as a carrier and the metal component is loaded onto the surface of the semi-coke by ultrasonic assisted pressure impregnation method. A series of Mn_Cu adsorbents are prepared. The method has simple operation and low cost. The prepared Mn_Cu adsorbent can achieve stable 80% NO denitrification rate and 90% SO2 desulfurization rate. Among them, the penetration time and the penetration capacity of NO can reach 300 min and 10.07 mg/g, while the penetration time and the penetration capacity of SO2 can reach 184 min and 14.62 mg/g when the removal efficiency of SO2 is above 90%.
【技术实现步骤摘要】
一种干法脱硫脱硝用的半焦负载锰铜吸附剂制备方法
本专利技术涉及一种环保领域，具体是一种干法脱硫脱硝用的半焦负载锰铜吸附剂制备方法。
技术介绍
传统的联合处理工艺中，湿法脱硫后产生的废水和废气，需要较多的设备和较复杂的工艺，提高了投资和运行成本，同时也降低了系统安全性，其排放的大量可溶性盐，目前还没有有效的解决方法。目前的干法或半干法技术与SO2发生的气固相或气液相反应，反应效果不理想。SNCR技术中由于在高温反应区喷入了10-20％的氨或尿素溶液，导致该反应区内温度急速下降，引起了该区域的温度梯度不均匀，进而降低了烟气的脱硝效率，目前SNCR技术的作用效率仅为30-50％；SCR技术采用的催化剂易中毒且价格也通常比较昂贵，其原料成本能够占据SCR系统总成本的20-40％，达到了运行成本的四成到五成。干法脱硫技术的问题在于吸附剂的循环利用和吸附产物的利用，吸附剂的循环利用一直是不断研究的方向，其中，高能电子氧化法脱硫效率能达到90％以上，但是它耗能巨大，不适宜应用；荷电干式脱硫法技术污染较小，但脱硫效率不高；放电等离子催化法利用等离子体中的高能产生催化作用，这种强还...
【技术保护点】
1.一种干法脱硫脱硝用的半焦负载锰铜吸附剂制备方法，其步骤包括：(1)取一定量的半焦，破碎后筛选出10‑20目的颗粒，再经去离子水浸泡冲洗，放入烘箱内自然烘干得到未负载金属组分的半焦，待用；(2)配置一定锰铜摩尔比的硝酸锰和硝酸铜溶液至100ml；(3)称取20g未负载金属组分的半焦，其体积约为20ml，与100ml的硝酸锰和硝酸铜溶液混合搅拌均匀后，放入超声高压釜内，升温200℃后恒温，同时开启超声装置超声，超声完成后自然冷却至室温并取出样品；(4)将步骤(3)的样品放入烘箱进行烘干，之后将样品放入石英管中，在氮气保护下焙烧，即制得Mn‑Cu吸附剂。
【技术特征摘要】
1.一种干法脱硫脱硝用的半焦负载锰铜吸附剂制备方法，其步骤包括：(1)取一定量的半焦，破碎后筛选出10-20目的颗粒，再经去离子水浸泡冲洗，放入烘箱内自然烘干得到未负载金属组分的半焦，待用；(2)配置一定锰铜摩尔比的硝酸锰和硝酸铜溶液至100ml；(3)称取20g未负载金属组分的半焦，其体积约为20ml，与100ml的硝酸锰和硝酸铜溶液混合搅拌均匀后，放入超声高压釜内，升温200℃后恒温，同时开启超声装置超声，超声完成后自然冷却至室温并取出样品；(4)将步骤(3)的样品放入烘箱进行烘干，之后将样品放入石英管中，在氮气保护下焙烧，即制得Mn-Cu吸附剂。2.根据权利要求1所述的一种一种干法脱硫脱硝用的半焦负载锰铜吸附剂...
【专利技术属性】
技术研发人员：宁平，李波，王学谦，