The invention provides a preparation method and application of a modified fly ash carbon composite material, which belongs to the technical field of solid waste recycling. Specifically, the activated fly ash is calcined at high temperature after mixing with a small amount of biomass, sulfate and alkali. The modified fly ash carbon composite material prepared by the invention has the advantages of wide source of raw materials and low price, and realizes high added value of solid waste. The composite material prepared by the invention has the advantages of less material consumption and remarkable adsorption effect for organic pollutants in coal-fired flue gas.
【技术实现步骤摘要】
一种改性粉煤灰-炭复合材料的制备方法及应用
本专利技术属于固体废物资源化
，特别涉及一种改性粉煤灰-炭复合材料的制备方法及应用。
技术介绍
我国能源结构主要以煤炭为主，煤炭燃烧过程中排放大量污染物，据相关报道，燃煤电厂产生的VOCs排放量约占总人为源的37％，是大气中挥发性有机物重要来源之一，对生态环境和人体健康构成了重大威胁。近些年，随着国家对生态环境保护的高度重视，开发燃煤过程有机污染物控制技术，将为燃煤电厂实现污染物全面控制提供技术支撑，具有广泛的应用前景和显著的社会、环境效益。粉煤灰是火力发电厂等燃煤锅炉排放的固体废物，具有良好的吸附性能和混凝过滤作用。近几年，国内外对粉煤灰的研究重点是通过制备吸附剂和催化剂处理废水污染。在废气处理方面，主要集中在NO、SO2和CO2等污染物的研究，而对有机污染物的研究报道较少。利用粉煤灰进行有机污染物的处理，能达到“以废制废”、节约成本的目的。但粉煤灰本身存在比表面积较小，吸附容量不高等不足。因此，通过改性方式提高粉煤灰吸附特性是一种有效的方法。生物炭是由生物质在惰性气体气氛下通过缓慢热解方式制备而成，其具有比表面...
【技术保护点】
1.一种改性粉煤灰‑炭复合材料的制备方法，其特征在于：该制备方法包括以下步骤：步骤一.粉煤灰的预处理：将粉煤灰洗涤、过滤，放置于90～120℃烘箱中烘干，过80～120目筛，取筛下粉煤灰，密封备用；步骤二.改性粉煤灰‑炭的制备：将步骤一筛选得到的粉煤灰与碳酸钠混合均匀，放置于管式炉中，经800～900℃焙烧1～3h，冷却后分别加入生物质、硫酸盐和碱；然后以固液比w/v为1:10～12(g/mL)的比例加入去离子水，放置于40～90℃水浴锅中搅拌6～12h，置于烘箱中烘干，放入管式炉中600～800℃焙烧1～5h，水洗至中性，烘干后得到改性粉煤灰‑炭复合材料。
【技术特征摘要】
1.一种改性粉煤灰-炭复合材料的制备方法，其特征在于：该制备方法包括以下步骤：步骤一.粉煤灰的预处理：将粉煤灰洗涤、过滤，放置于90～120℃烘箱中烘干，过80～120目筛，取筛下粉煤灰，密封备用；步骤二.改性粉煤灰-炭的制备：将步骤一筛选得到的粉煤灰与碳酸钠混合均匀，放置于管式炉中，经800～900℃焙烧1～3h，冷却后分别加入生物质、硫酸盐和碱；然后以固液比w/v为1:10～12(g/mL)的比例加入去离子水，放置于40～90℃水浴锅中搅拌6～12h，置于烘箱中烘干，放入管式炉中600～800℃焙烧1～5h，水洗至中性，烘干后得到改性粉煤灰-炭复合材料。2.根据权利要求1所述一种改性粉煤灰-炭复合材料的制备方法，其特征在于：所述粉煤灰为燃煤电厂排放出的粉煤灰。3.根据权利要求1所述一种改性粉煤灰-炭复合材料的制备方法，其特征在于步...