The invention provides a new environmental chromium corundum brick and its production process. The chromium corundum brick comprises the following components: compact corundum: 30-50 parts, brown corundum: 20-40 parts, chromium oxide powder: 15-25 parts, alpha alumina powder: 10-15 parts, fused mullite: 10-15 parts, titanium dioxide powder: 5-10 parts, silicon carbide powder: 5-10 parts, electrolyte: 1-5 parts, organic binder: 1-5 parts, organic binder: 1-5 parts. Binder: 1 - 5 copies. The chromium corundum brick has reasonable composition design, friendly production process, high strength, high temperature resistance, strong corrosion resistance, long service life, low production cost and good economic benefit.
【技术实现步骤摘要】
一种新型环保铬刚玉砖及其生产工艺
本专利技术属于铬刚玉砖生产
，具体地，涉及一种新型环保铬刚玉砖及其生产工艺。
技术介绍
铬刚玉砖（chromecorundumbrick）是指含Cr2O3的刚玉质耐火制品。在高温下，Cr2O3与Al2O3形成连续固溶体，因而铬刚玉制品的高温性能优于纯刚玉制品。用于石化工业气化炉的铬刚玉砖应为低硅、低铁、低碱、高纯度，还要具有较高的密度和强度。应用较多的铬刚玉制品，Cr2O3含量大多在9%~15%范围内。主要矿物组成为α-Al2O3-Cr2O3固溶体。次要矿物组成为少量复合尖晶石(或不含复合尖晶石)、氧化铬含量为1%～30%的耐火砖。有熔铸铬刚玉砖和烧结铬刚玉砖两种。一般情况下铬刚玉砖就是指烧结铬刚玉砖。铬刚玉砖（chromecorundumbrick）是指含Cr2O3的刚玉质耐火制品。在高温下，Cr2O3与Al2O3形成连续固溶体，因而铬刚玉制品的高温性能优于纯刚玉制品。用于石化工业气化炉的铬刚玉砖应为低硅、低铁、低碱、高纯度，还要具有较高的密度和强度。应用较多的铬刚玉制品，Cr2O3含量大多在9%~15%范围内。对于铬刚玉...
【技术保护点】
1.一种新型环保铬刚玉砖，其特征在于，所述铬刚玉砖包括如下重量份的成分：致密刚玉：30~50份，棕刚玉：20~40份，氧化铬粉：15~25份，α‑氧化铝粉：10~15份，电熔莫来石：10~15份，二氧化钛粉：5~10份，碳化硅粉：5~10份，解胶剂：1~5份，有机粘结剂：1~5份，结合剂：1~5份。
【技术特征摘要】
1.一种新型环保铬刚玉砖，其特征在于，所述铬刚玉砖包括如下重量份的成分：致密刚玉：30~50份，棕刚玉：20~40份，氧化铬粉：15~25份，α-氧化铝粉：10~15份，电熔莫来石：10~15份，二氧化钛粉：5~10份，碳化硅粉：5~10份，解胶剂：1~5份，有机粘结剂：1~5份，结合剂：1~5份。2.根据权利要求1所述的新型环保铬刚玉砖，其特征在于，所述铬刚玉砖包括如下重量份的成分：致密刚玉：40~50份，棕刚玉：30~40份，氧化铬粉：15~20份，α-氧化铝粉：12~15份，电熔莫来石：13~15份，二氧化钛粉：5~8份，碳化硅粉：6~10份，解胶剂：1~3份，有机粘结剂：1~4份，结合剂：2~5份。3.根据权利要求1所述的新型环保铬刚玉砖，其特征在于，所述铬刚玉砖包括如下重量份的成分：致密刚玉：40份，棕刚玉：30份，氧化铬粉：20份，α-氧化铝粉：13份，电熔莫来石：14份，二氧化钛粉：7份，碳化硅粉：8份，解胶剂：3份，...
【专利技术属性】
技术研发人员：戴永善，
申请(专利权)人：新沂北美高科耐火材料有限公司，
类型：发明
国别省市：江苏,32