转印片、装饰片及装饰品制造技术

【课题】本发明专利技术的目的在于提供一种能够赋予光滑且柔软的触感的转印片和装饰片。另外，本发明专利技术的目的在于提供一种难以产生箔毛刺的转印片。另外，本发明专利技术的目的在于提供一种具有光滑且柔软的触感的装饰品。【解决手段】转印片，构成为在基体片上至少依次层积有含有颗粒且表面粗糙度Ra为0.15‑1.0μm的脱模层、由电离放射线固化性的聚氨酯系树脂构成且马氏硬度为2.0‑40.0N/mm

Transfer prints, decorative films and ornaments

[Subject] The object of the present invention is to provide a transfer sheet and an ornamental sheet capable of giving a smooth and soft touch. In addition, the object of the present invention is to provide a transfer sheet which is difficult to generate foil burrs. In addition, the object of the present invention is to provide an ornament with smooth and soft touch. [Solution] The transfer sheet consists of a demoulding layer with particles and a surface roughness of Ra of 0.15 to 1.0 um, a polyurethane resin curable by ionizing radiation and a hardness of 2.0 to 40.0N/mm.

【技术实现步骤摘要】
【国外来华专利技术】转印片、装饰片及装饰品
本专利技术涉及转印片、装饰片及装饰品。
技术介绍
在便携终端的壳体、车辆内饰部件等树脂成形品中，根据近年来消费者的多样的需求，除了外观上的装饰以外，还被赋予了各种功能性。其中之一是光滑且润泽的触感。这样的触感，可以通过将基体片、含有颗粒的脱模层、由电离放射线固化性树脂构成的保护层以及粘合层依次层积而成的转印片转印到树脂成形品的表面上而获得(例如，参照专利文献1)。该转印片，在构成脱模层的树脂中混合一定量的一定大小的颗粒并涂布在基体片上，在其上形成保护层，因此在转印后在保护层表面形成由颗粒产生的凹凸。通过该凹凸形状，能够对树脂成形品表面赋予光滑且润泽的触感。另外，这样的触感，例如可以通过使用将上述转印片转印到支承片等被转印物而成的装饰片并进行注塑成形而获得。现有技术文献专利文献专利文献1：日本特开2015-182302号公报
技术实现思路
专利技术所要解决的问题但是，在以往的转印片及装饰片中，在保护层中不使用柔软的材料而仅通过保护层的表面形状来赋予触感，因此存在虽然能够获得光滑的触感但是不能获得柔软的触感的问题。另外，在转印片中，即使在保护层中使用了柔软的材料的情况本文档来自技高网...

【技术保护点】
1.一种转印片，是在基体片上至少依次层积有脱模层、保护层、粘合层的转印片，所述脱模层含有颗粒且表面粗糙度Ra为0.15‑1.0μm，所述保护层由电离放射线固化性的聚氨酯系树脂构成且马氏硬度为2.0‑40.0N/mm2，所述粘合层含有丙烯酸系树脂。

【技术特征摘要】
【国外来华专利技术】2016.06.17 JP 2016-120942;2016.06.17 JP 2016-120941.一种转印片，是在基体片上至少依次层积有脱模层、保护层、粘合层的转印片，所述脱模层含有颗粒且表面粗糙度Ra为0.15-1.0μm，所述保护层由电离放射线固化性的聚氨酯系树脂构成且马氏硬度为2.0-40.0N/mm2，所述粘合层含有丙烯酸系树脂。2.根据权利...

【专利技术属性】
技术研发人员：河合由里香，西垣光，松本笃昌，大崎雅人，
申请(专利权)人：NISSHA株式会社，
类型：发明
国别省市：日本,JP