The invention provides a preparation method of core-shell structure of nano-copper/graphene quantum dots. Ultrasound treatment of copper precursor compounds with graphene quantum dots/graphene quantum dots with small layers of graphene which are close to the size of graphene quantum dots (GQDs) yields a uniformly dispersed mixture, and the core-shell structure of nano-copper/graphene QDs is obtained by adding reductant. The method adopts graphene quantum dots and small size graphene to encapsulate copper nanoparticles more easily. The core-shell structure formed by the method can effectively protect nano-copper, and can be carried out at room temperature and atmospheric environment. The requirement for equipment is low, and it is suitable for industrial or laboratory operation.
【技术实现步骤摘要】
一种纳米铜/石墨烯量子点核壳结构的制备方法
本专利技术涉及新材料制备领域，尤其涉及一种纳米铜/石墨烯量子点核壳结构的制备方法。
技术介绍
贵金属资源有限且价格昂贵，制约了其大规模地推广与应用，资源丰富且较为廉价的铜纳米颗粒被视为贵金属纳米颗粒理想的替代者。但是，目前合成铜纳米颗粒的方法有一定局限性，例如铜纳米颗粒尺寸的均匀性差，易团聚，不宜长时间保存，露出在空气中时很容易在表面形成氧化膜，导致铜纳米颗粒在实际应用中受到很大的限制。使用石墨烯包裹铜纳米颗粒可避免氧化膜的形成，且石墨烯包覆铜纳米颗粒核壳结构复合材料的催化效率比贵金属纳米颗粒提高很多，也可制备成导电墨水取代银墨水，应用于触摸屏、显示屏等领域。中国专利技术专利(CN201410690635.9)《一种纳米铜/石墨烯复合材料及其制备方法与应用》与中国专利技术专利(CN201310068516.5)《石墨烯基纳米铜润滑油添加剂的制备方法》制备的纳米铜/石墨烯复合材料具有物相单一、形貌可控、负载量可控、纳米铜粒径小且均匀分布在石墨烯纳米层表面等特点，但是并不能形成核壳结构，对纳米铜进行保护。曲良体等利用铜纳米颗...
【技术保护点】
1.一种纳米铜/石墨烯量子点核壳结构的制备方法，包括如下步骤：(1)将铜前驱体化合物与石墨烯量子点/尺寸接近石墨烯量子点的小片层石墨烯加入溶剂中，超声处理得到均匀分散的混合液；(2)将还原剂加入到混合液中进行搅拌反应，得到纳米铜/石墨烯量子点核壳结构。
【技术特征摘要】
1.一种纳米铜/石墨烯量子点核壳结构的制备方法，包括如下步骤：(1)将铜前驱体化合物与石墨烯量子点/尺寸接近石墨烯量子点的小片层石墨烯加入溶剂中，超声处理得到均匀分散的混合液；(2)将还原剂加入到混合液中进行搅拌反应，得到纳米铜/石墨烯量子点核壳结构。2.根据权利要求1所述的制备方法，其特征在于，步骤(1)中的铜前驱体化合物为氯化铜、硫酸铜的一种或者混合物。3.根据权利要求1所述的制备方法，其特征在于，步骤(1)中的石墨烯量子点尺寸在40-100nm内，其边缘及表面修饰有含氧基团，通过控制用于制备石墨烯量子点的石墨纳米颗粒尺寸，以及对制备得到的...
【专利技术属性】
技术研发人员：苗中正，田利，苗中明，
申请(专利权)人：盐城师范学院，
类型：发明
国别省市：江苏,32