The invention provides a method for preparing perovskite quantum dots coated with polymers, which includes the following steps: providing perovskite quantum dots, dispersing the perovskite quantum dots in solvents to form perovskite quantum dot solutions, in which the ligands on the surface of the perovskite quantum dots include thiocarboxylic acid ligands; adding polymer monomers and photoinitiation into the perovskite quantum dot solutions. Under ultraviolet irradiation with water vapor content less than 30%, a polymer-coated perovskite quantum dot is formed, in which the polymer monomer is an unsaturated polymer monomer containing amino group.
【技术实现步骤摘要】
聚合物包覆的钙钛矿量子点及其制备方法
本专利技术属于钙钛矿量子点制备
，尤其涉及一种聚合物包覆及其钙钛矿量子点的制备方法。
技术介绍
近几年来无机钙钛矿量子点成为“量子点家族”中一位备受关注和研究的新成员。无机钙钛矿量子点具有窄的荧光发射半峰宽、高的荧光量子产率和易于在表面修饰各种功能基团的优势；且生物化学性能上也有着无可比拟的特性，如良好的生物兼容性，低细胞毒性，这些优越光学的性质使得无机钙钛矿量子点在生化和光学分析检测等领域中具有广泛应用前景。目前，常见的钙钛矿量子点，合成过程中一般以硫羧酸类配体作为稳定剂，如2-巯基乙酸、3-巯基丙酸、巯基丁二酸、4-巯基丁酸等。用硫羧酸类化合物作为配体包覆得到的钙钛矿量子点，量子点表面电离出来的羧酸根负离子能形成同性相斥的作用，使得量子点不发生团聚而沉淀。然而，在酸性条件下，羧酸难以电离，因此，钙钛矿量子点表面几乎不带电荷，钙钛矿量子点仍然容易发生聚沉。此外，小分子的硫羧酸类稳定剂虽然能一定程度分散于量子点表面，但很难将钙钛矿量子点表面完全包覆，由此形成的表面缺陷会导致发光效率的下降。
技术实现思路
本专利技术的目的在于...
【技术保护点】
1.一种聚合物包覆的钙钛矿量子点的制备方法，其特征在于，包括以下步骤：提供钙钛矿量子点，将所述钙钛矿量子点分散在溶剂中形成钙钛矿量子点溶液，其中，所述钙钛矿量子点表面的配体包括硫羧酸类配体；在所述钙钛矿量子点溶液中加入聚合物单体和光引发剂，在紫外照射条件下，硫羧酸类配体中巯基取代的碳原子形成自由基并使聚合物单体发生光聚合，制备得到聚合物包覆的钙钛矿量子点，其中，所述聚合物单体为含有氨基的不饱和聚合物单体。
【技术特征摘要】
1.一种聚合物包覆的钙钛矿量子点的制备方法，其特征在于，包括以下步骤：提供钙钛矿量子点，将所述钙钛矿量子点分散在溶剂中形成钙钛矿量子点溶液，其中，所述钙钛矿量子点表面的配体包括硫羧酸类配体；在所述钙钛矿量子点溶液中加入聚合物单体和光引发剂，在紫外照射条件下，硫羧酸类配体中巯基取代的碳原子形成自由基并使聚合物单体发生光聚合，制备得到聚合物包覆的钙钛矿量子点，其中，所述聚合物单体为含有氨基的不饱和聚合物单体。2.如权利要求1所述的聚合物包覆的钙钛矿量子点的制备方法，其特征在于，所述紫外照射条件下制备聚合物包覆的钙钛矿量子点的步骤中，制备环境中的水蒸气的体积分数低于30％。3.如权利要求1所述的聚合物包覆的钙钛矿量子点的制备方法，其特征在于，所述钙钛矿量子点与所述聚合物单体的用量比为20～50g:1L。4.如权利要求1所述的聚合物包覆的钙钛矿量子点的制备方法，其特征在于，所述聚合物单体为N-(3-二甲氨基丙基)甲基丙烯酰胺、4-氨基苯乙烯、4-二甲基氨基苯乙烯、乙烯亚胺、α-氨基丙烯酸、a-乙酰氨基丙烯酸和丙烯酸二甲氨基乙酯中的至少一种。5.如权利...
【专利技术属性】
技术研发人员：邓承雨，杨一行，钱磊，谢相伟，
申请(专利权)人：TCL集团股份有限公司，
类型：发明
国别省市：广东,44