The invention provides a water-based ultra-thin expansion steel structure fire retardant coating, which comprises the following components: 40~60 parts of acrylic emulsion, 10~30 parts of polyvinyl acetate emulsion, 4~8 parts of ammonium polyphosphate, 2~6 parts of pentaerythritol, 8~16 parts of expanded perlite, 0.4 to 0.8 parts of wetting dispersing agent, 0.3 to 0.6 parts of leveling agent, 2~6 parts of film forming aid, and 20 of modified calcium sulfate whisker. Among them, the modified calcium sulfate whisker is mainly prepared by calcium sulfate whisker, nano-titanium dioxide and aluminate coupling agent. The fire retardant coating has the characteristics of thin coating and excellent thermal insulation and fire retardant performance.
【技术实现步骤摘要】
水性超薄型膨胀钢结构防火涂料
本专利技术属于涂料
，具体涉及一种水性超薄型膨胀钢结构防火涂料。
技术介绍
相对于混凝土，钢结构在材料性能、经济效益、环境保护上具有明显的优势，被广泛应用于大跨度结构、超高层建筑、普通住宅及办公楼等，正逐步成为建筑的主流材料。然而，钢结构的防火性能差，在很大程度上制约了其发展。理论上，钢结构在全负荷下无法保持静态平衡的临界温度是528℃。建筑物一旦发生火灾，10分钟内火场温度就可达到700℃以上，裸露的钢结构在火灾发生的10分钟内即达到临界温度，便会产生塑性形变而失去承重能力，进而引起钢结构建筑的迅速坍塌。防火涂料可对钢结构起到有效的防火保护作用，可延缓钢结构在火灾中的升温，延长其到达临界温度的时间，可以为消防人员灭火和人们逃生争取时间，具有重要的现实意义。钢结构防火涂料具有涂覆厚度薄、饰面型好等特点，被广泛应用于钢结构中，在遇火受热条件下能快速膨胀到原始厚度的十几倍甚至数十倍，在钢结构表面形成一层致密的隔热保温层，阻止热量向钢结构传递，起到提高耐火极限的功能。然而，相对于其他非膨胀型防火涂料，现有的钢结构防火涂料在发泡膨胀初期...
【技术保护点】
1.一种水性超薄型膨胀钢结构防火涂料，其特征在于，按照重量份数，包括以下组分：丙烯酸乳液40～60份、聚醋酸乙烯乳液10～30份、聚磷酸铵4～8份、双季戊四醇2～6份、膨胀珍珠岩8～16份、润湿分散剂0.4～0.8份、流平剂0.3～0.6份、成膜助剂2～6份及改性硫酸钙晶须20～30份；其中，所述改性硫酸钙晶须主要由硫酸钙晶须、纳米二氧化钛与铝酸酯偶联剂制备得到。
【技术特征摘要】
1.一种水性超薄型膨胀钢结构防火涂料，其特征在于，按照重量份数，包括以下组分：丙烯酸乳液40～60份、聚醋酸乙烯乳液10～30份、聚磷酸铵4～8份、双季戊四醇2～6份、膨胀珍珠岩8～16份、润湿分散剂0.4～0.8份、流平剂0.3～0.6份、成膜助剂2～6份及改性硫酸钙晶须20～30份；其中，所述改性硫酸钙晶须主要由硫酸钙晶须、纳米二氧化钛与铝酸酯偶联剂制备得到。2.根据权利要求1所述的水性超薄型膨胀钢结构防火涂料，其特征在于，所述改性硫酸钙晶须的制备方法为：将硫酸钙晶须加入到3～6wt％的马来酸溶液中进行超声分散，升温至80℃～90℃，然后再加入纳米二氧化钛与铝酸酯偶联剂，搅...
【专利技术属性】
技术研发人员：汪琦，
申请(专利权)人：安庆市泽烨新材料技术推广服务有限公司，
类型：发明
国别省市：安徽,34