The invention discloses a polythiophene conductive additive, which is composed of the following raw materials: ferric trichloride hexahydrate 3 4, thiophene 100 110, dicarboxydimethyl ammonium bromide 0.7 1, conductive dispersion 16 20, aluminium stearate 2 3, vinyl bisstearate amide 1 2, trichloroisocyanuric acid 2 3. The silane coupling agent Kh550 is used to modify acetylene carbon black to improve the performance. The surface activity of acetylene carbon black was then doped with trichloroisocyanuric acid, the thiophene monomer was polymerized under the action of oxidant, and the dispersing liquid of activated carbon black was added in the process of polymerization, thus effectively improving the dispersion compatibility of carbon black between polythiophene, and improving the stability strength and conductive stability of the product.
【技术实现步骤摘要】
一种聚噻吩导电添加剂及其制备方法
本专利技术属于导电材料领域，具体涉及一种聚噻吩导电添加剂及其制备方法。
技术介绍
导电聚合物聚噻吩，有良好的光电性能，与其它共轭高分子如聚苯胺、聚吡咯等相比有更好的化学稳定性。尤其是其衍生物聚(3，4-乙撑二氧噻吩)(PEDOT)具有易制备、电化学活性高，良好的导电性和环境稳定性，掺杂后相对高比容量等优点，在超级电容器和锂离子电极材料方面有较大的应用。但是它也和其他导电聚合物一样，不可避免地存在骨架结构易破坏，容量衰减非常明显的情况，因此，如何提高其导电稳定性，增强骨架结构的稳定性是目前研究的重点。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种聚噻吩导电添加剂及其制备方法。为实现上述目的，本专利技术采用以下技术方案：一种聚噻吩导电添加剂，其特征在于，它是由下述重量份的原料组成的：六水三氯化铁3-4、噻吩100-110、双癸基二甲基溴化铵0.7-1、导电分散液16-20、硬脂酸铝2-3、乙烯基双硬脂酸酰胺1-2、三氯异氰尿酸2-3。所述的导电分散液是由下述重量份的原料组成的：乙炔炭黑14-20、N-甲基吡咯烷酮3...
【技术保护点】
1.一种聚噻吩导电添加剂，其特征在于，它是由下述重量份的原料组成的：六水三氯化铁3‑4、噻吩100‑110、双癸基二甲基溴化铵0.7‑1、导电分散液16‑20、硬脂酸铝2‑3、乙烯基双硬脂酸酰胺1‑2、三氯异氰尿酸2‑3。
【技术特征摘要】
1.一种聚噻吩导电添加剂，其特征在于，它是由下述重量份的原料组成的：六水三氯化铁3-4、噻吩100-110、双癸基二甲基溴化铵0.7-1、导电分散液16-20、硬脂酸铝2-3、乙烯基双硬脂酸酰胺1-2、三氯异氰尿酸2-3。2.根据权利要求1所述一种聚噻吩导电添加剂，其特征在于，所述的导电分散液是由下述重量份的原料组成的：乙炔炭黑14-20、N-甲基吡咯烷酮30-40、硅烷偶联剂Kh5500.3-1、吡啶硫酮锌1-2。3.根据权利要求2所述的一种聚噻吩导电添加剂，其特征在于，所述的导电分散液的制备方法，包括以下步骤：(1)取吡啶硫酮锌，加入到其重量7-9倍的无水乙醇中，搅拌均匀，升高温度为60-65℃，加入乙炔炭黑，保温搅拌20-30分钟，得炭黑分散液；(2)取硅烷偶联剂Kh550，加入到上述炭黑分散液中，超声1-2小时，蒸馏除去乙醇，...