The invention relates to a method for removing tungsten from molybdate solution containing tungsten, including steps: 1) adjusting the pH value of molybdate solution containing tungsten to 1-3 with phosphoric acid solution to obtain acidified solution; 2) adding potassium salt solution or ammonium salt solution to acidified solution for stirring reaction, solid-liquid separation, obtaining tungsten slag and molybdenum solution, and WO3 content in solution can be as low as 50 ppm, solid. High efficiency separation of molybdenum and tungsten has been achieved. The process is short, the operation is simple, the loss of molybdenum is small, the production cost is low, the operation is simple, and it is easy to realize industrial production.
【技术实现步骤摘要】
一种从含钨的钼酸盐溶液中除钨的方法
本专利技术涉及稀有金属冶金领域
，尤其涉及一种从含钨的钼酸盐溶液中除钨的方法。
技术介绍
钼的高温强度、硬度和刚性大，抗热耐震性能和耐腐蚀性能好，导热、导电性能优良，这些性能使钼、钼合金以及钼化工产品在各个领域用途广泛。随着资源的开发利用，优质辉钼矿资源日益匮乏，复杂钼资源越来越多，其中高钨辉钼矿已成为当前钼冶金中非常重要的原料。随着科技的不断进步，为获得性能优异的钼制品，对其中杂质的控制要求越来越高，尤其钨是钼产品中严格控制的杂质元素。而钨钼的性质非常相似，二者的分离非常困难，若不采取单独的除钨工序，则难以制备出合格的钼产品。在处理高钨辉钼矿等复杂钼资源时，从钼酸盐溶液中高效除去钨已经成为钼冶金中一个亟待解决的难题。目前，从钼酸盐溶液中除钨的方法主要有吸附沉淀法、离子交换法和溶剂萃取法等。专利CN101531735A提出一种离子交换树脂除钨的方法，通过调整溶液pH至6.5～7.5，使钼酸盐溶液中的钨优先聚合成仲钨酸根离子，再用离子交换树脂优先吸附钨的性质来除去钨。然而，在调整溶液pH的过程中，钼酸根也会发生聚合，当溶液中...
【技术保护点】
1.一种从含钨的钼酸盐溶液中除钨的方法，其特征在于，包括以下步骤：1)用磷酸溶液将含钨的钼酸盐溶液的pH值调整至1～3得到酸化后的溶液；2)将钾盐溶液或铵盐溶液加入到酸化后的溶液中，固液分离后，得到除钨渣和含钼溶液。
【技术特征摘要】
1.一种从含钨的钼酸盐溶液中除钨的方法，其特征在于，包括以下步骤：1)用磷酸溶液将含钨的钼酸盐溶液的pH值调整至1～3得到酸化后的溶液；2)将钾盐溶液或铵盐溶液加入到酸化后的溶液中，固液分离后，得到除钨渣和含钼溶液。2.根据权利要求1所述的从含钨的钼酸盐溶液中除钨的方法，其特征在于，在步骤1)中，所述磷酸溶液的浓度为1～10mol/L。3.根据权利要求1所述的从含钨的钼酸盐溶液中除钨的方法，其特征在于，在步骤2)中，所述钾盐溶液中的钾盐为氯化钾、硫酸钾、硝酸钾和磷酸钾中的一种或多种。4.根据权利要求1所述的从含钨的钼酸盐溶液中除钨的方法，其特征在于，在步骤2)中，所述铵盐溶液中的铵盐为氯化铵、硫酸铵、硝酸铵和磷酸二氢铵中的一种或多种。5.根据权利要...
【专利技术属性】
技术研发人员：刘旭恒，赵中伟，任慧川，陈星宇，李江涛，
申请(专利权)人：中南大学，
类型：发明
国别省市：湖南,43