The invention relates to the technical field of antioxidant compositions, in particular to an antioxidant composition for reducing the content of polyols and aldehydes, including hindered phenolic antioxidants and phosphite antioxidants; the hindered phenolic antioxidant is a mixture of hindered phenol I with type I structure and hindered phenol II with type II structure; the weight fraction of the hindered phenolic antioxidant is a composition. The weight fraction of the phosphite antioxidant is 30.80% of the weight of the composition. The invention can not only inhibit the growth of aldehydes in polyols, reduce the content of volatile and high odor substances in polyols, but also improve the thermal oxidation stability of polyols, thereby improving the oxidation resistance of polyurethane products.
【技术实现步骤摘要】
降低多元醇醛类物质含量的抗氧剂组合物
本专利技术涉及抗氧剂组合物
，特别是涉及一种降低多元醇醛类物质含量的抗氧剂组合物。
技术介绍
聚氨酯全称为聚氨基甲酸酯，是通过异氰酸酯与多元醇反应来制备。由于聚氨酯制品具有良好的性能，而被广泛应用于建筑、家具、床垫、汽车行业等领域。近年来，随着人们生活水平的不断提高，人们的环保意识也逐渐增强，聚氨酯制品存在的挥发性、高气味等问题已成为限制其应用的重要因素。聚氨酯制品中挥发性、高气味物质主要来自于合成原料多元醇，而多元醇的气味主要来自于甲醛、乙醛、丙醛类等醛酮类物质，这不仅会影响聚氨酯制品的使用，而且还会对人体健康构成危害。目前，降低多元醇中醛酮类物质的方法有很多，然而，现有的方法存在很多缺陷，如工艺复杂，生产成本非常高，效率低，能耗大等。另外，聚氨酯制品在生产、存储、使用过程中受空气中氧气的作用非常容易氧化，发生黄变，而影响其物理性能和机械性能。尤其在受热、紫外线照射、或有杂质存在下，会加速聚氨酯泡沫的氧化降解，导致聚氨酯制品的物理性能和机械性能大幅度下降，从而影响聚氨酯制品的正常使用。为了抑制、阻止或延迟聚氨酯制品氧化...
【技术保护点】
1.降低多元醇醛类物质含量的抗氧剂组合物，其特征在于：包括受阻酚类抗氧剂和亚磷酸酯类抗氧剂；所述受阻酚类抗氧剂为具有式Ⅰ结构的受阻酚Ⅰ与具有式Ⅱ结构的受阻酚Ⅱ的混合物；
【技术特征摘要】
1.降低多元醇醛类物质含量的抗氧剂组合物，其特征在于：包括受阻酚类抗氧剂和亚磷酸酯类抗氧剂；所述受阻酚类抗氧剂为具有式Ⅰ结构的受阻酚Ⅰ与具有式Ⅱ结构的受阻酚Ⅱ的混合物；其中R1为C12-C22的烷基或酯基；其中n为1、2、3或4，R2为C4-C20的烷基；所述受阻酚类抗氧剂的重量分数为组合物重量的20-70％，所述亚磷酸酯类抗氧剂的重量分数为组合物重量的30-80％。2.根据权利要求1所述的降低多元醇醛类物质含量的抗氧剂组合物，其特征在于：所述亚磷酸酯类抗氧剂为聚(二丙二醇)苯基亚磷酸酯、双(2,4-二叔丁基苯酚)季戊四醇二亚磷酸酯、双(2,6-二叔丁基-4-甲基苯基)季戊四醇二磷酸酯、具有式Ⅲ结构的亚磷酸酯类抗氧剂中的一种或几种混合物，其中R3、R4、R5为具有下式结构的烷基化芳基：其中R6、R7、R8为H或C1-C6烷基。3.根据权利要求1所述的降低多元醇醛类物质含量的抗氧剂组合物，其特征在于：该组合物在常温下为液态。4.根据权利要求1所述的降低多元醇醛类物质含量的抗氧剂组合物...
【专利技术属性】
技术研发人员：段世锋，石珺，
申请(专利权)人：襄阳亚克化学有限公司，
类型：发明
国别省市：湖北,42