The invention discloses a raw material formula for lard white porcelain, which is made of the following raw materials according to their components: silicon dioxide 47.7-56.8 phr, aluminium oxide 20.8-22.4 phr, iron oxide 0.01-0.086 phr, calcium oxide 3.2-4 phr, magnesium oxide 3.03-3.42 phr, potassium oxide 3.66-5.66 phr, sodium oxide 0.26-1.06 phr, titanium dioxide 0.01-0.05 phr, barium oxide 4.1-4.5 phr, holmium oxide 1.06 phr phr. The invention changes the present situation that lard white porcelain can only be obtained by occasional pit change. According to the raw material formula of the invention, lard white porcelain can be prepared by conventional firing method, and can be produced on a large scale, which has great historical significance for the ceramic industry.
【技术实现步骤摘要】
一种猪油白瓷的原料配方
:本专利技术涉及一种陶瓷的原料配方,尤其涉及一种猪油白瓷的原料配方。
技术介绍
:德化窑以生产白瓷著称于世,其品质精良是古代其他窑口所不能比拟的,其产品备受世人喜爱,而称为“中国白”(BlancdeChine)。明代是德化窑白瓷生产的又一个高峰期,产品以其品质的绝对优势占领国际市场而大量外销。由于原产地配方的不同,使德化窑白瓷产品的质地和釉面色泽效果也不同。在民间叫法和学术上,明代德化窑白瓷被分为“孩儿红”、“象牙白”、“猪油白”、“葱根白”、“鹅绒白”等,其中“猪油白”是明代德化窑白瓷中的极品,要在一定气氛下才偶然产生,得者甚少,传世就更少。
技术实现思路
:本专利技术的目的是提供一种猪油白瓷的原料配方,其可通过常规工艺烧制而成,所得的猪油白瓷数量较多、品质精良。本专利技术的猪油白瓷的原料配方,由以下原料按组分制成:二氧化硅25~75份,三氧化二铝10~35份,三氧化二铁0.005~0.2份,氧化钙1~6份,氧化镁1~5份,氧化钾2~8份,氧化钠0.1~2份,二氧化钛0.005~0.1份,氧化钡2~6份,氧化锶0.5~4份。优选地,所述的二氧化硅47.7~56.8份,三氧化二铝20.8~22.4份,三氧化二铁0.01~0.086份,氧化钙3.2~4份,氧化镁3.03~3.42份,氧化钾3.66~5.66份,氧化钠0.26~1.06份,二氧化钛0.01~0.05份,氧化钡4.1~4.5份,氧化锶1.06~1.96份。本专利技术的猪油白瓷的原料配方,改变了现有的只能通过偶尔的窖变而得到猪油白瓷的现状,按照本专利技术的原料配方便可通过常规烧 ...
【技术保护点】
1.一种猪油白瓷的原料配方,其特征在于由以下原料按组分制成:二氧化硅25~75份,三氧化二铝10~35份,三氧化二铁 0.005~0.2 份,氧化钙 1~6份,氧化镁1~5份,氧化钾2~8份,氧化钠0.1~2份,二氧化钛0.005~0.1份,氧化钡2~6份,氧化锶0.5~4份。
【技术特征摘要】
1.一种猪油白瓷的原料配方,其特征在于由以下原料按组分制成:二氧化硅25~75份,三氧化二铝10~35份,三氧化二铁0.005~0.2份,氧化钙1~6份,氧化镁1~5份,氧化钾2~8份,氧化钠0.1~2份,二氧化钛0.005~0.1份,氧化钡2~6份,氧化锶0.5~4份。2.如权利要求1所述的一种猪油白瓷...