The invention relates to the technical field of coated cloth, in particular to a hydrophobic coated cotton fabric, including a cotton base cloth, which is woven by cotton thread and evenly compounded with a hydrophobic coating on two surfaces of the cotton base cloth. The hydrophobic coating is a mixture of polyurethane resin and epoxy resin, and the mass ratio of the two coatings is 3 to 5:1. The thickness of the hydrophobic coating on the surface of the cotton base cloth is 0.3. _0.5 mm, hydrophobic coating is divided into two coatings. The thickness of the first coating is 0.1 0.2 mm, the thickness of the second coating is 0.2 0.4 mm, and the interval between the two coatings is 30 minutes. The hydrophobic coated cotton fabric obtained by the invention can effectively improve the hydrophobicity on the surface of cotton fabric through reasonable structure and process design, and has superior performance and high stability.
【技术实现步骤摘要】
一种疏水涂层棉质面料
本专利技术涉及涂层布
，尤其是一种疏水涂层棉质面料。
技术介绍
纺织用品是人们休闲生活必不可少的东西，伴随着各种使用的需求，这些物品会被使用在各种各样的场合，当然包括户外，由于传统的户外纺织用品日晒牢度不够高，在经过一段时间的日晒、洗涤后会出现泛黄、褪色的现象，会影响这些纺织用品的使用和外观，重则作废，造成一种不必要的浪费，所以一种户外防晒的面料就显得尤为重要；同时现有的防晒面料透气效果差，因此人们穿上这种面料后，容易产生异味，并滋生细菌，满足不了人们的需要。另外，传统的制作服装本体的面料不具有超疏水性能。
技术实现思路
本专利技术的目的是为了解决上述技术的不足而提供一种能有效提升疏水性能的疏水涂层棉质面料。为了达到上述目的，本专利技术所设计的一种疏水涂层棉质面料，包括棉质基布，棉质基布由棉线编织而成，在棉质基布的两个表面均匀复合有疏水涂层，其中疏水涂层为聚氨酯树脂与环氧树脂混合物，且两者的质量比例为3-5：1，疏水涂层在棉质基布表面的厚度为0.3-0.5mm，疏水涂层分为两次涂覆，第一次涂覆的厚度为0.1-0.2mm，第二次涂覆的厚度为0...
【技术保护点】
1.一种疏水涂层棉质面料，其特征是：包括棉质基布，棉质基布由棉线编织而成，在棉质基布的两个表面均匀复合有疏水涂层，其中疏水涂层为聚氨酯树脂与环氧树脂混合物，且两者的质量比例为3‑5：1，疏水涂层在棉质基布表面的厚度为0.3‑0.5mm，疏水涂层分为两次涂覆，第一次涂覆的厚度为0.1‑0.2mm，第二次涂覆的厚度为0.2‑0.4mm，两次涂覆的间隔时间为30min。
【技术特征摘要】
1.一种疏水涂层棉质面料，其特征是：包括棉质基布，棉质基布由棉线编织而成，在棉质基布的两个表面均匀复合有疏水涂层，其中疏水涂层为聚氨酯树脂与环氧树脂混合物，且两者的质量比例为3-5：1，疏水涂层在棉质基布表面的厚度为0.3-0.5mm，疏水涂层分为两次涂覆，第一次涂覆的...