An oil for nylon spinning consists of 5 7 fatty alcohol polyoxyethylene ether, 8 11 sebacate, 1 3 fatty alcohol polyoxyethylene phosphate potassium salt, 3 5 polyethylene glycol oleic acid, 8 10 secondary alkyl alcohol polyoxyethylene ether, 4 6 octanol phosphate triethanolamine salt, 0.5 1.5 anti-spatter agent, 88 cosmetic grade white oil. The invention has the following beneficial effects: (1) The oil agent of the invention has good heat dissipation and heat resistance, and is suitable for high speed spinning. (2) The oiling agent of the invention has good smoothness, small friction coefficient of fibers and contact objects, can reduce the damage and breakage caused by friction in spinning, and maintain stable spinning tension. (3) The oiling agent of the invention has good antistatic property, clustering property, wear resistance and emulsifying stability.
【技术实现步骤摘要】
一种锦纶纺丝用油剂
本专利技术涉及一种锦纶纺丝用油剂，属于化纤油剂领域。
技术介绍
锦纶油剂应该具有如下性能和作用：（1）平滑性：在纺丝卷绕过程中，使丝条能顺利而平整地绕到丝筒上，减少设备和纤维之间的摩擦；另一方面，在拉伸时，应能使丝条顺利地从丝筒上退绕下来，不发生乱丝现象；同时，能使牵伸均匀进行，使牵伸丝的新表面得到保护。（2）抗静电性：锦纶在纺丝生产过程中，由于丝条与金属导辊表面摩擦，以及丝条之间在运动中进行摩擦易产生静电现象，因此造成纤维蓬松、毛丝、断头、缠绕罗拉、粘附设备等现象。油剂中的抗静电剂便可中和纤维上的静电并帮助导电，其次，油剂还能增强纤维的润滑性，吸湿性，减少静电产生。（3）集束性：在卷绕的拉伸过程中，油剂能使丝条具有适合的粘性，增加纤维之间的抱合力，使多根纤维集束在一起，共同经受拉伸，以获得良好的拉伸效果。（4）耐高温性能：锦纶在拉伸后有同步的热辊高稳定型，因此要求油剂要有优良的耐热性和稳定性，即油剂在高温下不分解、不冒烟、不滴油、不结焦。（5）润湿渗透性：锦纶在高速纺过程中，锦纶丝束与油剂接触时间极短，为保证在接触的瞬间油剂分子能均匀地附着在...
【技术保护点】
1.一种锦纶纺丝用油剂，其特征在于，按照质量份包括以下组成：脂肪醇聚氧乙烯醚 5‑7份，癸二酸二辛酯8‑11份，脂肪醇聚氧乙烯磷酸酯钾盐 1‑3份，聚乙二醇油脂酸 3‑5份，仲烷基醇聚氧乙烯醚 8‑10份，辛醇磷酸酯三乙醇胺盐 4‑6份，抗飞溅剂 0.5‑1.5份，化妆级白油 88‑92份。
【技术特征摘要】
1.一种锦纶纺丝用油剂，其特征在于，按照质量份包括以下组成：脂肪醇聚氧乙烯醚5-7份，癸二酸二辛酯8-11份，脂肪醇聚氧乙烯磷酸酯钾盐1-3份，聚乙二醇油脂酸3-5份，仲烷基醇聚氧乙烯醚8-10份，辛醇磷酸酯三乙醇胺盐4-6份，抗飞溅剂0.5-1.5份，化妆级白油88-92份。2.根据权利要求1所述的锦纶纺丝用油剂，其特征在于，所述油剂按照质量份包括以下组成：脂肪醇聚氧乙烯醚5.6-6份，癸二酸二辛酯9-10份，脂肪醇聚氧乙烯磷酸酯钾盐1.8-2.4份，聚乙二醇油脂酸4.1-4.6份，仲烷基醇聚氧乙烯醚8.5-9.5份，辛醇...
【专利技术属性】
技术研发人员：张存生，
申请(专利权)人：浙江新胜油脂科技有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。