A medium and high concentration phosphating solution is composed of 70 90g/L of Mazhifu salt, 2.8 11.5g/L of phosphoric acid, 3 5g/L of iron chips and water. The total acidity of the phosphating solution is 70 to 90 points, and the free acidity is 14 to 18 points, and the ratio of the total acidity to the free acidity is 4:1 to 6:1. The preparation method: firstly, 60_80g/L of Mazhifu salt was weighed and dissolved in 70 C water. After dissolution, water was supplemented and heated to boiling; secondly, it was cooled to 70 C and feldspar was added 3_5g/L. After 30_45 minutes of reaction, 2.8_7.2g/L of phosphoric acid was added to sample analysis and acidity was adjusted to the target value. It has good applicability, simple composition and easy preparation.
【技术实现步骤摘要】
一种中高溶度磷化液及其制备方法
本专利技术涉及一种磷化液，特别涉及一种中高溶度磷化液及其制备方法。
技术介绍
磷化液可用于钢铁的表面处理。钢铁在含有锰、锌的磷化液中进行磷化处理后，可在钢铁的表面生成均匀致密的结晶磷化膜，该膜可提高钢铁的抗磨性能，延长钢铁的使用寿命，因而磷化液被广泛应用于飞机、汽车、变速箱、分动箱以及各种齿轮上零件的表面处理。中国专利公开号：CN101787524B，专利公开日：2011年11月02日，专利名称：《一种薄层耐磨磷化液及其配制方法》，该专利技术提到一种磷化液，该磷化液的组成成分及其含量为：马日夫盐45-50g/L，磷酸1-2ml/L，硝酸镍2-4g/L，硝酸钙2-10g/L，硝酸锌0.5-2g/L，铁屑3-5g/L，柠檬酸1-3g/L，用以调整游离酸度的碳酸锰适量，其余量为水，磷化液的总酸度为45-50点，游离酸度6.5-7.5点，且总酸度与游离酸度之比为6：1-7：1。配制时，先称取马日夫盐40-45g/L放入70℃的水中溶解，溶解完后补充水，然后加热至沸腾，再冷却至70℃时加铁屑3-5g/L，反应30-45分钟后加磷酸0.5-2....
【技术保护点】
1.一种中高浓度磷化液，其特征在于所述磷化液的组成成分及其含量为：马日夫盐70‑90g/L，磷酸2.8‑11.5g/L，铁屑3‑5g/L，余量为水；所述磷化液的总酸度为70‑90点，游离酸度为14‑18点，且总酸度与游离酸度之比为4：1‑6：1。
【技术特征摘要】
1.一种中高浓度磷化液，其特征在于所述磷化液的组成成分及其含量为：马日夫盐70-90g/L，磷酸2.8-11.5g/L，铁屑3-5g/L，余量为水；所述磷化液的总酸度为70-90点，游离酸度为14-18点，且总酸度与游离酸度之比为4：1-6：1。2.根据权利要求1所述的一种中高溶度磷化液，其特征在于：所述的磷酸以85％磷酸添加到磷化液中。3.根据权利要求1所述的一种中高浓度磷化液，其特征在于：所述的磷化液还包含有用以调整游离酸度的碳酸锰。4.根据权利要求1-3中任一项所述的一种中高浓...
【专利技术属性】
技术研发人员：张春晖，胡佳阳，刘刚，张辉，顾宝军，骆银，马建成，
申请(专利权)人：武汉船用机械有限责任公司，
类型：发明
国别省市：湖北,42