The invention belongs to the technical field of waterproofing coatings, and proposes a non-curable modified asphalt waterproofing coating and its preparation method, including asphalt 30 45, thermoplastic styrene-butadiene rubber 8 15, thermoplastic styrene-butadiene rubber powder 1 3, silicone rubber powder 2 7, solid paraffin 5 15, soybean oil 30 45, epoxy soybean oil 1 3, reduced second or third-line Oil 2 3, solvent oil 15 25, cyclic acid. Anhydride compatibilizer 0.5 0.8. The invention also provides a preparation method of non-curable modified asphalt waterproof coating. Through the above technical scheme, the problem of poor heat resistance and low temperature flexibility of the existing rubber asphalt non-curable waterproof coating is solved.
【技术实现步骤摘要】
一种非固化改性沥青防水涂料及其制备方法
本专利技术属于防水涂料
，涉及一种非固化改性沥青防水涂料及其制备方法。
技术介绍
橡化沥青非固化防水涂料在施工后即使长时间放置也不会固化，保持防水材料的原有性能，能够提高防水层的寿命。其“永不固化”性能主要是以它的固含量来决定。其他防水涂料施工时混合水或其他溶剂使其拥有施工性，但施工后随着溶剂的挥发防水层固化。橡化沥青非固化防水涂料其本身的固含量为99％以上，施工时采用专用设备，无需添加溶剂，因此施工后即使经过长时间也不会固化并保持其性能。但是现有技术中的非固化改性沥青防水涂料在使用过程中存在耐热性较差的问题，在温度较高时，流动性大；且低温柔性较差，从而使非固化改性沥青防水涂料的使用受到了限制，限制了使用环境和施工环境。CN13937407B公开了非固化橡胶沥青防水涂料，此涂料由沥青、橡胶、分散剂、增粘剂和填料组成，该涂料在-30℃无裂纹，不脆断，产品80℃不流淌。但这种程度的耐热性和低温柔性仍不能满足一些恶劣环境的使用要求。因此，专利技术一种具备优异耐热性和低温柔性的橡化沥青非固化防水涂料还是很有必要的。
技术实现思路
...
【技术保护点】
1.一种非固化改性沥青防水涂料，其特征在于：包括以下质量配比的组分：沥青30‑45，热塑性丁苯橡胶8‑15，热塑性丁苯橡胶粉末1‑3，硅橡胶粉末2‑7，固体石蜡5‑15，大豆油30‑45，环氧大豆油1‑3，减二线油或减三线油2‑3，溶剂油15‑25，环状酸酐型相容剂0.5‑0.8。
【技术特征摘要】
1.一种非固化改性沥青防水涂料，其特征在于：包括以下质量配比的组分：沥青30-45，热塑性丁苯橡胶8-15，热塑性丁苯橡胶粉末1-3，硅橡胶粉末2-7，固体石蜡5-15，大豆油30-45，环氧大豆油1-3，减二线油或减三线油2-3，溶剂油15-25，环状酸酐型相容剂0.5-0.8。2.根据权利要求1所述的一种非固化改性沥青防水涂料，其特征在于：所述热塑性丁苯橡胶粉末的粒度在90-120，硅橡胶粉末30-60。3.根据权利要求1所述的一种非固化改性沥青防水涂料，其特征在于：所述溶剂...
【专利技术属性】
技术研发人员：赵云涛，孙井龙，李允宽，马伯伦，秦冬彪，
申请(专利权)人：固安金盾时代建筑防水材料有限公司，
类型：发明
国别省市：河北,13
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。