The invention discloses a quick setting early strength castable for blast furnace tapping ditch, which comprises brown corundum 20%-40%, silicon carbide superfine powder 20%-35%, Portland cement 5%-11%, sulphoaluminate cement 3%-7%, sand 2%-10%, gravel 4%-8%, water reducer 0.10%-0.25%, siliceous clinker 5%-10%, modified asphalt 2%-6%, sericite 5%-8%, explosion-proof fiber 1%-2% according to weight percentage. The quick-setting and early-strength castable used for blast furnace tapping trench has high fluidity, good working performance, self-compacting performance and quick-setting and early-strength performance, which makes the strength of the tapping trench high, reduces the maintenance frequency and reduces the cost.
【技术实现步骤摘要】
用于高炉出铁沟的速凝早强浇注料
本专利技术涉及耐火材料
，尤其涉及一种用于高炉出铁沟的速凝早强浇注料。
技术介绍
高炉出铁沟承担着高炉铁水与渣的排放，关系到高炉的稳定运行。出铁沟的制作，需要将浇注料浇筑于出铁沟模具中，不烘烤或者短时间烘烤以后即可投入使用。为保证时效性，现有的浇注料内添加了添加剂以实现快速凝结干燥。但是凝结时间短，制备的出铁沟的强度则较低，导致出铁沟使用过程中出现裂纹，维修养护频率增加，增加成本。
技术实现思路
为解决现有技术中，用于高炉出铁沟的速凝早强浇注料存在的凝结快但强度低的技术问题，本专利技术的技术方案如下：本专利技术中的用于高炉出铁沟的速凝早强浇注料，按重量百分比包括棕刚玉20％～40％、碳化硅超细粉20％～35％、硅酸盐水泥5％～11％、硫铝酸盐水泥3％～7％、砂2％～10％、碎石4％～8％、减水剂0.10％～0.25％、硅质熟料5％～10％、改质沥青2％～6％、绢云母5％～8％、防爆纤维1％～2％。在一种优选的实施方式中，按重量百分比包括棕刚玉40％、碳化硅超细粉20％、硅酸盐水泥6％、硫铝酸盐水泥4％、砂2％、碎石4％、减水剂0....
【技术保护点】
1.用于高炉出铁沟的速凝早强浇注料，其特征在于，按重量百分比包括棕刚玉20%～40%、碳化硅超细粉20%～35%、硅酸盐水泥5%～11%、硫铝酸盐水泥3%~7%、砂2%～ 10%、碎石4%～8%、减水剂0.10%～0.25%、硅质熟料5%～10%、改质沥青2%～6%、绢云母5%～8%、防爆纤维1%~2%。
【技术特征摘要】
1.用于高炉出铁沟的速凝早强浇注料，其特征在于，按重量百分比包括棕刚玉20%～40%、碳化硅超细粉20%～35%、硅酸盐水泥5%～11%、硫铝酸盐水泥3%~7%、砂2%～10%、碎石4%～8%、减水剂0.10%～0.25%、硅质熟料5%～10%、改质沥青2%～6%、绢云母5%～8%、防爆纤维1%~2%。2.根据权利要求1所述的用于高炉出铁沟的速凝早强浇注料，其特征在于，按重量百分比包括棕刚玉40%、碳化硅超细粉20%、硅酸盐水泥6%、硫铝酸盐水泥4%、砂2%、碎石4%、减水剂0.10%、硅质熟料10%、改质沥青6%、绢云母6%、防爆纤维1.9%。3.根据权利要求1所述的用于高炉出铁沟的速凝早强浇注料，其特征在于，按重量百分比包括棕刚玉30%、碳化硅超细粉35%、硅酸盐水泥7%、硫铝酸盐水泥3%、砂5%、碎石6%、减水剂0.25%、硅质熟料5%、改质沥青2%、绢云母5%、防爆纤维1.75%。4.根据权利要求1所述的用于高炉出铁沟的速凝早强浇注料，其特征在于，按重量百分比包括棕刚玉20%、碳化硅超细粉30%、硅酸盐水泥11%、硫铝酸盐水泥7%、砂7...
【专利技术属性】
技术研发人员：张志成，佘凤娅，佘亚锋，司志刚，
申请(专利权)人：长兴明天炉料有限公司，
类型：发明
国别省市：浙江,33