The invention provides a method for preparing a three-dimensional network structure SiC_Fe based composite material. Compared with the prior art, the invention adopts an organic foam impregnation method to prepare a three-dimensional network structure silicon carbide ceramic preform with uniform structure and excellent mechanical properties, and the three-dimensional network structure SiC_Fe based composite material produced by the atmospheric pressure casting method has excellent compressive strength and abrasion resistance. The wear resistance of SiC_Fe matrix composites with three-dimensional network structure can reach 7.9 times of that of cast iron.
【技术实现步骤摘要】
一种三维网络结构SiC_Fe基复合材料的制备方法
本专利技术涉及一种陶瓷材料及制品领域，具体是一种三维网络结构SiC_Fe基复合材料的制备方法。
技术介绍
众多研究者在网络结构复合材料方面有深入的研究，但多数研究对象是以轻金属(Al、Mg和Cu等)为基体，以重金属钢铁为基体制备三维网络结构陶瓷金属基复合材料的研究并不多，多数集中在陶瓷颗粒增强金属基复合材料方面。而大多数制备出的陶瓷颗粒增强金属基复合材料中陶瓷颗粒与金属基体呈现的是一种简单的机械结合，陶瓷颗粒被金属基体包裹，在摩擦磨损过程中金属基体被磨损一部分后，陶瓷颗粒凸显出来承载以后的载荷。此时陶瓷颗粒处于独立状态，在外力的作用下很容易发生脱落或者断裂，脱落的陶瓷颗粒沿着摩擦方向进入摩擦表面对后期的磨损影响很大。
技术实现思路
本专利技术为了解决上述现有技术所存在的不足之处，提供了一种三维网络结构复合材料的制备方法，能够制备出性能优异的三维网络结构复合材料。一种三维网络结构SiC_Fe基复合材料的制备方法，包括以下步骤：1)取聚氨酯泡沫放入20％的氢氧化钠溶液，加热至50℃并保温6h，然后用清水清洗浸泡后的聚氨酯泡...
【技术保护点】
1.一种三维网络结构SiC_Fe基复合材料的制备方法，其特征在于，包括以下步骤：1)取聚氨酯泡沫放入20％的氢氧化钠溶液，加热至50℃并保温6h，然后用清水清洗浸泡后的聚氨酯泡沫，风干备用；2)取木质素磺酸铵和聚羧酸盐按比例溶解于去离子水中，快速搅拌5min，配制成盐溶液；3)取碳化硅粉末、活性氧化铝、二氧化硅微粉和添加剂放置在水泥搅拌机中慢速搅拌5min，使其混合均匀，然后将步骤2)中的盐溶液倒入水泥搅拌机中，充分搅拌30min，最后在水泥搅拌机中加入一定量的消泡剂，搅拌5min，制成碳化硅陶瓷浆料；4)将碳化硅陶瓷浆料均匀涂覆在步骤1)中预处理过的聚氨酯泡沫上，然后用压...
【技术特征摘要】
1.一种三维网络结构SiC_Fe基复合材料的制备方法，其特征在于，包括以下步骤：1)取聚氨酯泡沫放入20％的氢氧化钠溶液，加热至50℃并保温6h，然后用清水清洗浸泡后的聚氨酯泡沫，风干备用；2)取木质素磺酸铵和聚羧酸盐按比例溶解于去离子水中，快速搅拌5min，配制成盐溶液；3)取碳化硅粉末、活性氧化铝、二氧化硅微粉和添加剂放置在水泥搅拌机中慢速搅拌5min，使其混合均匀，然后将步骤2)中的盐溶液倒入水泥搅拌机中，充分搅拌30min，最后在水泥搅拌机中加入一定量的消泡剂，搅拌5min，制成碳化硅陶瓷浆料；4)将碳化硅陶瓷浆料均匀涂覆在步骤1)中预处理过的聚氨酯泡沫上，然后用压辊挤压机挤出多余的浆料，并通过空气压力移除堵塞在孔洞的浆料，制得三维网络结构碳化硅陶瓷素坯，保持三维网络结构碳化硅陶瓷素坯在空气中自然风干24h，然后在110℃干燥箱中干燥12h，将干燥后的三维网络结构碳化硅陶瓷素坯在高温烧结炉中进行热处理...
【专利技术属性】
技术研发人员：王宏德，
申请(专利权)人：江西鸿司远特种泡沫材料有限公司，
类型：发明
国别省市：江西,36