The invention discloses a graphite grooving and its preparation method, which is made by mixing wet material and powder, and the wet material is modified asphalt. The powder comprises the following components: graphite powder 50-60, bauxite 8-12, natural flake graphite powder 10, brown corundum 5-8 and silicon carbide 10-20, and the ratio of wet material to powder is 100:20-30. The graphite chute prepared by the special composition and the special production process has the characteristics of smooth surface, non-sticking molten iron, long service life, no environmental pollution in the production process and high production efficiency.
【技术实现步骤摘要】
一种石墨落槽及其制备方法
本专利技术涉及铁水浇注系统
，特别是一种导流铁水用的石墨落槽及其制备方法。
技术介绍
在金属铸造领域中，浇注是把熔融金属土等注入模具，进行金属部件的铸造。现有的铁水浇注加工一般是先将高温处理后的铁水通过落槽倒入铁水包中，然后通过人工搬运至对应的浇注工位上进行浇注操作，这其中使用的落槽一般为石墨落槽。石墨落槽的结构大多为整体为弧形、截面U型的结构；其材质为石墨材质，多采用碳素厂生产的石墨电极通过手工锯切、打孔、穿钢丝、5-6块对接、粘合、打磨后制成。采用传统工艺制备石墨落槽存在以下缺陷：1）采用手工锯切的石墨电极表面凸凹不平，无法保证几何精度，对接茬口比较明显，造成石墨产品尺寸不一，表面粗糙；2）组织疏松、强度低、耐高温铁水冲击性差，一般使用寿命20小时，使用寿命短，更换频繁；3）由于采用胶粘工艺，产品有较大的胶味，造成生产环境空气污染；4）粘合完成后，需要对石墨落槽砖进行修整才能使用，生产一个石墨落槽的平均时间为2h左右，效率低下；5）由于石墨材质自身的限制，石墨落槽无法机械化生产；6）石墨落槽砖在生产过程中会对生产现场造成严重的石...
【技术保护点】
1.一种石墨落槽，其特征在于，所述石墨落槽由湿料和粉料混合后制成，所述湿料为改质沥青；所述粉料包括以下重量份数的组分：石墨粉50~60份，铝矾土8~12份，天然鳞片石墨粉10份，棕刚玉5~8份，碳化硅10~20份；湿料与粉料的比例为100:20~30。
【技术特征摘要】
1.一种石墨落槽，其特征在于，所述石墨落槽由湿料和粉料混合后制成，所述湿料为改质沥青；所述粉料包括以下重量份数的组分：石墨粉50~60份，铝矾土8~12份，天然鳞片石墨粉10份，棕刚玉5~8份，碳化硅10~20份；湿料与粉料的比例为100:20~30。2.根据权利要求1所述的一种石墨落槽，其特征在于，所述石墨落槽由湿料和粉料混合后制成，所述湿料为改质沥青；所述粉料包括以下重量份数的组分：石墨粉55~60份，铝矾土8~10份，天然鳞片石墨粉10份，棕刚玉5~8份，碳化硅10~15份；湿料与粉料的比例为100:20~25。3.根据权利要求1所述的一种石墨落槽，其特征在于，所述石墨落槽由湿料和粉料混合后制成，所述湿料为改质沥青；所述粉料包括以下重量份数的组分：石墨粉60份，铝矾土10份，天然鳞片石墨粉10份，棕刚玉5份，碳化硅15份；所述湿料与粉料的比例为100:25。4.根据权利要求1所述的一种石墨落槽，其特征在于，所述石墨粉的粒度为0~3目，铝矾土的粒度为80~100目，天然鳞片...
【专利技术属性】
技术研发人员：刘伟，刘学艺，
申请(专利权)人：邯郸市永年区科冠铸造材料厂，
类型：发明
国别省市：河北,13