The invention discloses a method for producing nickel sulfate solution with nickel oxide as raw material. The steps include: (1) pretreatment of nickel oxide by hydrochloric acid or nitric acid; (2) dissolution of nickel oxide by sulfuric acid through step (1) and solid-liquid separation to obtain filtrate; (3) adding nickel oxide powder into filtrate obtained by step (2) to obtain nickel sulfate solution. The method adopts hydrochloric acid or nitric acid to pretreat the dense oxide film on the surface of nickel oxide to shorten the time of acid dissolving nickel oxide by sulfuric acid; uses nickel oxide powder to neutralize surplus acid without introducing impurities, and produces nickel sulfate solution with qualified impurities, which can be used as pre-evaporative liquid for evaporative crystallization of nickel sulfate without purifying and remo
【技术实现步骤摘要】
一种以氧化镍为原料生产硫酸镍溶液的方法
本专利技术属于湿法冶金
，具体涉及一种以氧化镍为原料生产硫酸镍溶液的方法。
技术介绍
工业生产硫酸镍的原料主要为金属镍、羰基镍、硫化镍矿、红土镍矿、粗制硫酸镍、电镀污泥及粗氢氧化镍等，但随着电池行业三元前驱体的快速发展，含镍原料供不应求。以红土矿为原料，喷雾热解法生成的氧化镍为圆球状颗粒，直径约为1-3mm，氧化镍主要用作搪瓷的密着剂和着色剂，陶瓷和玻璃的颜料，在磁性材料生产中用于生产镍锌铁氧体等，以及用作制造镍催化剂并在冶金、显像管中应用。由于表面有一层致密的氧化膜，使氧化镍处理困难，阻碍氧化镍在工业上应用；氧化镍处理液酸度较高，pH难以降低，如加入碱性物质中和，会引入新杂质，而直接蒸发结晶对现场不锈钢材质设备腐蚀严重。
技术实现思路
针对上述已有技术存在的不足，本专利技术提供一种以氧化镍为原料生产硫酸镍溶液的方法。本专利技术是通过以下技术方案实现的。一种以氧化镍为原料生产硫酸镍溶液的方法，其特征在于，所述方法步骤包括：(1)采用盐酸或者硝酸对氧化镍预处理；(2)采用硫酸溶解经步骤(1)得到的氧化镍，然后固液分离得到滤液...
【技术保护点】
1.一种以氧化镍为原料生产硫酸镍溶液的方法，其特征在于，所述方法步骤包括：（1）采用盐酸或者硝酸对氧化镍预处理；（2）采用硫酸溶解经步骤（1）得到的氧化镍，然后固液分离得到滤液；（3）将经步骤（2）得到的滤液中加入氧化镍粉，得到硫酸镍溶液。
【技术特征摘要】
1.一种以氧化镍为原料生产硫酸镍溶液的方法，其特征在于，所述方法步骤包括：（1）采用盐酸或者硝酸对氧化镍预处理；（2）采用硫酸溶解经步骤（1）得到的氧化镍，然后固液分离得到滤液；（3）将经步骤（2）得到的滤液中加入氧化镍粉，得到硫酸镍溶液。2.根据权利要求1所述的方法，其特征在于，所述步骤（1）氧化镍是以红土矿为原料制得的直径为1-3mm氧化镍颗粒。3.根据权利要求1所述的方法，其特征在于，所述步骤（1）首先采用盐酸或者硝酸对氧化镍进行预处理，其中，预处理温度为70-95℃，预处理时间为5-10min，然后固液分离，将经固液分离得到的固体用纯水常温洗涤，其中，纯水与经固液分离得到的固体按液固比为1-4:1，洗涤次数为3-6次，得到处理好的氧化镍。4.根据权利要求1所述的方法，其特征在于，所...
【专利技术属性】
技术研发人员：赵德，周佑明，麻在生，董存武，明键伟，沈艳玲，徐文兵，魏焘，
申请(专利权)人：金川集团股份有限公司，
类型：发明
国别省市：甘肃,62